Fatigue Property of Aviation Perspex
摘 要
通过对航空有机玻璃进行拉伸疲劳试验得到了不同应力水平下的拉伸疲劳S-N曲线以及条件疲劳强度, 研究了应力比对有机玻璃拉伸疲劳性能的影响。结果表明: 该有机玻璃在应力比为0.4, 0.1, -0.1条件下的疲劳强度分别为63.0,57.3, 48.4 MPa,其对应的拉伸疲劳S-N曲线随着应力比的增加整体上移; 在相同应力水平下, 应力比越大, 该有机玻璃的拉伸疲劳寿命越长。
Abstract
Tensile fatigue S-N curves and conditions fatigue strength of aviation perspex were obtained by tensile fatigue test and effect of stress ratio on fatigue properties of the aviation perspex was studied. The results show that the conditions fatigue strength of the perspex were 63.0, 57.3, 48.4 MPa under the condition of stress ratios were 0.4, 0.1, -0.4. The tensile fatigue S-N curves integrally moved up with the increase of stress ratio. Under the same stress level, specimens tested with higher stress ratio had longer fatigue life.
中图分类号 V216.3
所属栏目
基金项目
收稿日期 2011/3/22
修改稿日期
网络出版日期
作者单位点击查看
备注马丽婷(1977-),女,工程师,硕士。
引用该论文: MA Li-ting,CHEN Xin-wen,LI Lei. Fatigue Property of Aviation Perspex[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2011, 47(10): 612~614
马丽婷,陈新文,厉蕾. 航空有机玻璃的疲劳性能[J]. 理化检验-物理分册, 2011, 47(10): 612~614
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】高镇同, 蒋新桐, 熊峻江,等. 疲劳性能试验设计和数据处理[M]. 北京: 北京航空航天大学出版社, 1999:15-17.
【2】有机玻璃疲劳和断口图谱编委会. 有机玻璃疲劳和断口图谱[M]. 北京: 科学出版社,1987:136.
【2】有机玻璃疲劳和断口图谱编委会. 有机玻璃疲劳和断口图谱[M]. 北京: 科学出版社,1987:136.
相关信息