铜合金自来水表外壳破裂失效分析
Failure Analysis on Rupture of a Copper Alloy Water Meter Shell
摘 要
采用宏观检验、断口分析、能谱分析、金相检验以及化学成分分析等方法, 对某铜合金自来水表外壳在使用中发生破断开裂、造成泄露的原因进行了分析。结果表明: 该铜合金自来水表外壳在使用过程中发生破裂属于应力腐蚀破裂, 致使其发生应力腐蚀的原因主要与使用环境中含有硫化物有关。
破裂失效
硫化物
应力腐蚀
copper alloy water meter shell
rupture failure
sulfide
stress corrosion
Abstract
A copper alloy water meter shell ruptured and resulted in leakage in service, and the rupture reason was analyzed by means of macroscopic examination, fracture analysis, energy spectrum analysis, metallographic examination and chemical compositions analysis. The results show that the rupture of the copper alloy water meter shell in service was stress corrosion cracking which was mainly because there were sulfides in the service environment.
中图分类号 TG146.1+1
所属栏目
基金项目
收稿日期 2011/3/19
修改稿日期
网络出版日期
作者单位点击查看
备注戴维弟(1978-),男,高级工程师。
引用该论文: DAI Wei-di. Failure Analysis on Rupture of a Copper Alloy Water Meter Shell[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2011, 47(10): 656～658
戴维弟. 铜合金自来水表外壳破裂失效分析[J]. 理化检验－物理分册, 2011, 47(10): 656～658
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】丁慧麟, 辛智华. 实用铝合金、铜及其合金金相热处理和失效分析[M]. 北京:机械工程出版社,2008:567-568.
【2】美国金属学会. 金属手册[M]//失效分析与预防.第十卷.8版. 北京:机械工业出版社,1986:30.
【2】美国金属学会. 金属手册[M]//失效分析与预防.第十卷.8版. 北京:机械工业出版社,1986:30.
相关信息