40MnBH轧制钢棒裂纹分析
Analysis on Cracks in Rolled Bar of 40MnBH Steel
摘 要
通过夹杂物检验、蓝脆断口检验以及电子探针能谱分析对40MnBH钢表面出现轴向裂纹的成因进行了分析。结果表明: 裂纹是由连铸坯卷渣造成的。由于连铸拉速过高, 导致钢水在结晶器内形成紊流, 使得吸附了大量Al2O3和SiO2等脱氧产物的保护渣被卷入钢水中, 形成了连铸坯卷渣。
圆棒
裂纹
连铸保护渣
40MnBH steel
bar
crack
protective slag of continuous casting
Abstract
Axial cracking were found on the surface of some 40MnBH steel bars. Inclusion testing, blue brittleness testing and EPMA analysis were applied to analyse the cause of the cracks. The results showed that the cracks were caused by the protective slag entrapment of continuous casting. The high continuous casting speed led to the turbulent flow of the hot melt in the mould, resulting in the entrapment of the protective slag that has absorbed lots of deoxidation products, such as Al2O3 and SiO2.
中图分类号 TG335.6+2
所属栏目
基金项目
收稿日期 2011/2/28
修改稿日期
网络出版日期
作者单位点击查看
备注张文青(1974-), 女, 工程师, 学士。
引用该论文: ZHANG Wen-qing,YUN Yan-qing,CUI Hai-xia. Analysis on Cracks in Rolled Bar of 40MnBH Steel[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2011, 47(11): 710～712
张文青,云彦青,崔海霞. 40MnBH轧制钢棒裂纹分析[J]. 理化检验－物理分册, 2011, 47(11): 710～712
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘承军, 王云盛, 朱英雄,等.连铸保护渣的夹杂物吸收速率[J].钢铁研究学报, 2000(12):46-50.
【2】宋华. 连铸保护渣吸附夹杂能力浅析[J].黑龙江冶金, 2010,30(3):3-6.
【3】卢艳青, 张国栋, 姜茂发, 等. 连铸保护渣吸附Al2O3夹杂能力的研究[J].东北大学学报(自然科学版), 2010(31):539-541.
【2】宋华. 连铸保护渣吸附夹杂能力浅析[J].黑龙江冶金, 2010,30(3):3-6.
【3】卢艳青, 张国栋, 姜茂发, 等. 连铸保护渣吸附Al2O3夹杂能力的研究[J].东北大学学报(自然科学版), 2010(31):539-541.
相关信息