六角头螺栓断裂分析
Fracture Analysis of Hexagon Head Bolt
摘 要
采用宏观检验、断口分析、化学成分分析、力学性能测试及金相检验等方法对六角头螺栓的断裂原因进行了分析。结果表明: 六角头螺栓在酸洗和电镀工艺后未进行充分的去氢处理, 致使六角头螺栓中残存了较多的氢, 在应力和氢的共同作用下造成了螺栓的延迟断裂; 其次, 六角头螺栓表面存在0.2 mm左右的渗碳层, 使得螺栓表面硬度提高, 增加了螺栓的氢脆敏感性。
氢脆
断裂
渗碳
bolt
hydrogen embrittlement
fracture
carburization
Abstract
Macroscopic inspection, fracture analysis, chemical composition analysis, mechanical property testing and metallographic examination were conducted to clarify the reason for fracture in hexagon head bolt. The results showed that hydrogen was not removed after acid pickling and electroplate, the vestige of hydrogen in the bolt and the stress caused the hexagon head bolt to fracture. Furthermore, there was the carburized layer about 0.2 mm,it improved the hardness and increased the sensitivity of hydrogen embrittlement of bolt.
中图分类号 TH131.3
所属栏目
基金项目
收稿日期 2011/5/4
修改稿日期
网络出版日期
作者单位点击查看
备注孙国峰(1982-), 男, 工程师, 在职硕士。
引用该论文: SUN Guo-feng,YIN Qiang. Fracture Analysis of Hexagon Head Bolt[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2011, 47(11): 719～721
孙国峰,尹强. 六角头螺栓断裂分析[J]. 理化检验－物理分册, 2011, 47(11): 719～721
被引情况:
【1】谭晓舟, "螺纹有效旋合长度对螺栓拉力试验结果的影响",理化检验－物理分册 50, 351-352(2014)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】金蔚静.双头螺栓失效分析[J].理化检验-物理分册, 2003,39(5): 268-270.
【2】王大伦, 赵德寅, 郑佰芳.轴及紧固件的失效分析[M].北京: 机械工业出版社, 1988: 183-189.
【3】吴连生, 刘正义.机械装备失效分析图谱[M].广州: 广东科技出版社, 1990:273-275.
【4】黄志涛, 田文怀, 苏永安.普通碳素钢渗氮后的氢脆敏感性[J].理化检验-物理分册, 2010,46(7): 423-426.
【5】吴建国.氢气对金属材料之影响[J].材料导报, 2004,18(18): 119-120.
【6】卢洪.高强度螺栓断裂失效分析[J].福建工程学院学报, 2009,7(4): 341-343.
【2】王大伦, 赵德寅, 郑佰芳.轴及紧固件的失效分析[M].北京: 机械工业出版社, 1988: 183-189.
【3】吴连生, 刘正义.机械装备失效分析图谱[M].广州: 广东科技出版社, 1990:273-275.
【4】黄志涛, 田文怀, 苏永安.普通碳素钢渗氮后的氢脆敏感性[J].理化检验-物理分册, 2010,46(7): 423-426.
【5】吴建国.氢气对金属材料之影响[J].材料导报, 2004,18(18): 119-120.
【6】卢洪.高强度螺栓断裂失效分析[J].福建工程学院学报, 2009,7(4): 341-343.
相关信息