Test Methods and Susceptibility of Low-Cr Ferritic Stainless Steel to lntergranular Corrosin
摘 要
研究了爆炸复合板复层06Cr13R低铬铁素体不锈钢的晶间腐蚀敏感性测试方法及性能。结果表明: 电化学动电位扫描法(双环EPR法)适合用于爆炸复合板复层06Cr13R低铬铁素体不锈钢晶间腐蚀敏感性的检测, 其试验结果与草酸电解侵蚀法对应较好;06Cr13R低铬铁素体不锈钢的晶间腐蚀敏感性与铬-镍奥氏体不锈钢不同, 其晶间腐蚀敏感性出现在910 ℃正火处理后, 甚至强制吹风急冷条件下也无法避免, 而经过800 ℃退火处理后, 其晶间腐蚀敏感性可减轻。
Abstract
The test methods and susceptibility of explosion composite plate compound layer 06Cr13R low-Cr ferritic stainless steel to intergranular corrosion were studied. The results show that the double-loop EPR method was appropriate for evaluating the susceptibility of 06Cr13R low-Cr ferritic stainless steel to intergranular corrosion, which was consistent with the test results of oxalic acid electrdysis erosion method. The characteristics of intergranular corrosion of 06Cr13R low-Cr ferritic stainless steel was different from Cr-Ni austentic stainless steels. The susceptibility to intergranular corrosion occured after the normalizing treatment at 910 ℃, even forced air cooling, but it was alleviated after the annealing treatment at 800 ℃.
中图分类号 TG172
所属栏目
基金项目
收稿日期 2011/5/10
修改稿日期
网络出版日期
作者单位点击查看
备注查小琴(1975-),女,高级工程师,硕士。
引用该论文: ZHA Xiao-qin,WANG Xiao-hua. Test Methods and Susceptibility of Low-Cr Ferritic Stainless Steel to lntergranular Corrosin[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2011, 47(12): 741~743
查小琴,王小华. 低铬铁素体不锈钢晶间腐蚀敏感性的测试方法及性能[J]. 理化检验-物理分册, 2011, 47(12): 741~743
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】陆世英, 张廷凯, 杨长强, 等. 不锈钢[M].北京: 原子能出版社, 1995: 77-78.
【2】胡方坚, 伍玉琴, 钟祥玉, 等. 铁素体不锈钢的晶间腐蚀性能研究[J]. 腐蚀科学与防护技术,2009,21(2):110-112.
【3】DUFFAULT F, POUZET J P, LSOOMBE P. Potentiostatic study of structural modifications caused in a Ni-Cr-Fe alloy by heat treatment at 650 ℃[J]. Corrosion Science,1996,6(2):83-85.
【4】高中平, 陈范才, 赵常就. 动电位再活化法评价评价晶间腐蚀敏感性的各种判据[J]. 四川化工与腐蚀控制,1999,2(3):40-44.
【5】王凤平, 康万利, 敬和民. 腐蚀电化学原理、方法及应用[M]. 北京: 化学工业出版社,2007: 24.
【2】胡方坚, 伍玉琴, 钟祥玉, 等. 铁素体不锈钢的晶间腐蚀性能研究[J]. 腐蚀科学与防护技术,2009,21(2):110-112.
【3】DUFFAULT F, POUZET J P, LSOOMBE P. Potentiostatic study of structural modifications caused in a Ni-Cr-Fe alloy by heat treatment at 650 ℃[J]. Corrosion Science,1996,6(2):83-85.
【4】高中平, 陈范才, 赵常就. 动电位再活化法评价评价晶间腐蚀敏感性的各种判据[J]. 四川化工与腐蚀控制,1999,2(3):40-44.
【5】王凤平, 康万利, 敬和民. 腐蚀电化学原理、方法及应用[M]. 北京: 化学工业出版社,2007: 24.
相关信息