Fatigue Machine Design and Fatigue Life Test of Coiled Tubing
摘 要
采用自主设计研制的首台国产连续管弯曲疲劳试验机, 对某国产CT80钢级连续油管进行疲劳试验, 并对影响连续油管低周疲劳寿命的各种因素进行了研究。结果表明: 增加连续油管的壁厚、减小连续油管的外径、提高连续油管的屈服强度、减小管内压力、减少管体表面损伤以及提高连续油管焊接质量均能显著提高连续油管的弯曲疲劳寿命;
Abstract
Factors affecting the low cycle fatigue life of coiled tubing were studied by fatigue test to CT80 steel grade domestic coiled tubing with independently design first home-made coiled tubing bending fatigue machine. The results show that the fatigue life of the coiled tubing could be improved by increasing wall thickness, decreasing outside diameter, enhancing yield strength, dropping inner stress, reducing surface damage and improving welding quality of the coiled tubing.
中图分类号 TE931+.2
所属栏目 试验与研究
基金项目
收稿日期 2010/9/21
修改稿日期
网络出版日期
作者单位点击查看
备注毕宗岳(1962-), 男, 高级工程师, 博士。
引用该论文: BI Zong-yue,ZHANG Xiao-feng,ZHANG Wan-peng,JING Xiao-tian. Fatigue Machine Design and Fatigue Life Test of Coiled Tubing[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2012, 48(2): 79~82
毕宗岳,张晓峰,张万鹏,井晓天. 连续油管疲劳试验机设计与疲劳寿命试验[J]. 理化检验-物理分册, 2012, 48(2): 79~82
被引情况:
【1】张建伟,方健, "基于Test Suite TW软件研发的1000kN电子拉伸试验机低周疲劳测试方法",理化检验-物理分册 51, 539-541(2015)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李宗田.连续油管技术手册[M]. 北京: 石油工业出版社,2003:2-3.
【2】章传国.连续油管的发展[J]. 宝钢技术,2007(2):26-29.
【3】毕宗岳,井晓天,金时麟,等.连续油管性能研究与产品开发[J]. 石油矿场机械,2010,39(6):16-20.
【4】张运翘.连续油管的应力和寿命分析[J]. 石油矿场机械,1995,24(1):21-25.
【5】VAN ARNAM W D. Good coiled tubing welds,properly managed,do not break[C]//SPE/ICOTA Coiled Tubing Roundtable. Houston:SPE,2000:60694.
【6】TIPTON S M,MORAN D W,CHINSETHAGID C,et al. Quantifying the influence of surface defects on coiled tubing fatigue resistance[C]//SPE/ICOTA Coiled Tubing Conference. Houston:SPE,2002:74827.
【2】章传国.连续油管的发展[J]. 宝钢技术,2007(2):26-29.
【3】毕宗岳,井晓天,金时麟,等.连续油管性能研究与产品开发[J]. 石油矿场机械,2010,39(6):16-20.
【4】张运翘.连续油管的应力和寿命分析[J]. 石油矿场机械,1995,24(1):21-25.
【5】VAN ARNAM W D. Good coiled tubing welds,properly managed,do not break[C]//SPE/ICOTA Coiled Tubing Roundtable. Houston:SPE,2000:60694.
【6】TIPTON S M,MORAN D W,CHINSETHAGID C,et al. Quantifying the influence of surface defects on coiled tubing fatigue resistance[C]//SPE/ICOTA Coiled Tubing Conference. Houston:SPE,2002:74827.
相关信息