活塞式压缩机联轴器连接螺栓断裂原因分析
Analysis on Fracture Reason of Bolt on Piston Compressor Coupling
摘 要
某型号活塞式压缩机联轴器的连接螺栓在停车维修拆卸时发现断裂。通过化学成分分析、硬度测试、金相检验、断口分析及能谱分析对断裂原因进行了分析。结果表明: 螺栓根部存在结构不连续的退刀槽, 导致螺栓应力集中产生初始裂纹, 在长期服役后发生疲劳断裂。
连接螺栓
疲劳
应力集中
compressor
connecting bolt
fatigue
stress concentration
Abstract
A bolt on the piston compressor coupling was broken during their maintenance period. By means of chemical composition analysis, hardness testing, metallographic examination, fracture and energy spectrum analysis, the fracture reason was analyzed. The results showed that there was an undercut on the bolt root, which led to stress concentration to create initial crack. All of these led to bolt fatigue fracture after long-serving.
中图分类号 TH457
所属栏目 质量控制与失效分析
基金项目
收稿日期 2011/11/30
修改稿日期
网络出版日期
作者单位点击查看
备注石强(1987-), 男, 硕士研究生。
引用该论文: SHI Qiang,WANG Wei-qiang,TANG Jie,KONG Hao-yuan. Analysis on Fracture Reason of Bolt on Piston Compressor Coupling[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2012, 48(3): 203～205
石强,王威强,汤杰,孔浩源. 活塞式压缩机联轴器连接螺栓断裂原因分析[J]. 理化检验－物理分册, 2012, 48(3): 203～205
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】常用结构钢金相图谱编写组.常用结构钢金相图[M].北京:国防工业出版社,1982: 37-58.
【2】黄春峰.18Cr2Ni4WA钢热处理工艺研究[J].机械设计与制造工程, 1999,28(4):49-50.
【3】陈黄埔,金达增,邓赠杰,等.18Cr2Ni4WA钢不同组织形态及其机械性能之间关系[J].西安交通大学学报,1984,18(6):45-54.
【2】黄春峰.18Cr2Ni4WA钢热处理工艺研究[J].机械设计与制造工程, 1999,28(4):49-50.
【3】陈黄埔,金达增,邓赠杰,等.18Cr2Ni4WA钢不同组织形态及其机械性能之间关系[J].西安交通大学学报,1984,18(6):45-54.
相关信息