泵头体高强钢材料的力学性能
Mechanical Properties of High Strength Steel of Pump Head
摘 要
为了进一步研究泵头体高强钢25Cr2Ni4MoV和30CrNi2MoV的力学性能, 采用拉伸、冲击和裂纹尖端张开位移(CTOD)试验对其进行测试。结果表明: 材料在常温下具有较好的综合力学性能; 在静载荷条件下, 具有优良的断裂韧度。
高强钢
力学性能
裂纹尖端张开位移
断裂韧度
pump head
high strength steel
mechanical properties
crack tip opening displacement
fracture toughness
Abstract
In order to study the mechanical properties of high strength steel of pump head, the tensile test, impact test and the crack tip opening displacement (CTOD) experiment were did for 25Cr2Ni4MoV and 30CrNi2MoV steel. The results showed that the materials had good mechanical properties at room temperature and excellent fracture toughness under static load conditions.
中图分类号 TG142.33
所属栏目 试验与研究
基金项目
收稿日期 2011/9/27
修改稿日期
网络出版日期
作者单位点击查看
备注张太付(1984-), 男, 工学硕士。
引用该论文: ZHANG Tai-fu,LIU Shun-hong,XU Cai-qiang. Mechanical Properties of High Strength Steel of Pump Head[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2012, 48(5): 294～298
张太付,刘顺洪,徐才强. 泵头体高强钢材料的力学性能[J]. 理化检验－物理分册, 2012, 48(5): 294～298
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】袁祖耀.热处理温度对30CrNi2MoVA钢机械性能的影响[J].兵器材料科学与工程, 1985(10): 24-28.
【2】魏元春.奥氏体化温度对30CrNi2MoVA高强度钢淬火组织形态的影响[J].兵器材料科学与工程, 1980(1): 27-38.
【3】王静宜, 张子旺.30CrNi2MoVA钢等温淬火组织和机械性能的研究[J].金属热处理, 1986(9): 46-49.
【4】魏元春, 杨嘉, 张永秀.30CrNi2MoVA钢显微组织与机械性能的关系[J].兵器材料科学与工程, 1986(9):1-9.
【5】GB/T 2358-1994金属材料裂纹尖端张开位移试验方法[S].
【6】崔忠圻, 覃耀春.金属学与热处理[M].北京: 机械工业出版社, 2007.
【7】姜伟之, 赵时熙.工程材料的力学性能[M].北京: 北京航天航空大学出版社,2000.
【8】中国机械工程学会热处理分会.热处理手册——热处理质量控制和检验(第4卷)[M].北京: 机械工业出版社,2008.
【2】魏元春.奥氏体化温度对30CrNi2MoVA高强度钢淬火组织形态的影响[J].兵器材料科学与工程, 1980(1): 27-38.
【3】王静宜, 张子旺.30CrNi2MoVA钢等温淬火组织和机械性能的研究[J].金属热处理, 1986(9): 46-49.
【4】魏元春, 杨嘉, 张永秀.30CrNi2MoVA钢显微组织与机械性能的关系[J].兵器材料科学与工程, 1986(9):1-9.
【5】GB/T 2358-1994金属材料裂纹尖端张开位移试验方法[S].
【6】崔忠圻, 覃耀春.金属学与热处理[M].北京: 机械工业出版社, 2007.
【7】姜伟之, 赵时熙.工程材料的力学性能[M].北京: 北京航天航空大学出版社,2000.
【8】中国机械工程学会热处理分会.热处理手册——热处理质量控制和检验(第4卷)[M].北京: 机械工业出版社,2008.
相关信息