钢材相似显微组织的分析与鉴别
Analysis and Identification of Similar Microstructure of Steel
摘 要
在日常钢材的显微组织检验中, 由于网状铁素体和网状二次渗碳体、针状铁素体和针状渗碳体、马氏体及其回火产物(回火马氏体、回火屈氏体和回火索氏体)、未溶铁素体和先共析铁素体、淬火屈氏体和回火屈氏体等显微组织的显微特征非常相似, 容易出现误判。以常用碳钢为例, 运用显微组织观察、显微硬度测试、化学试剂侵蚀等金相检验的普通手段, 通过对显微组织形貌中的组织形态、分布、颜色进行直观比较, 总结归纳出了上述几种相似显微组织的鉴别方法, 以供金相检验人员参考。
鉴别
金相检验
similar microstructure
identification
metallographic examination
Abstract
In daily microstructure testing, because the mesh ferrite and mesh second cementite, needle ferrite and needle cementite, martensite and their tempered products (tempered martensite, tempered troostite and tempered sorbite), undissolved ferrite and proeutectoid ferrite, and quenched troostite and tempered troostite are very similar and difficultly identified. With carbon steels as examples, by means of observing microstructure, microhardness testing and chemical reagents erosion, the shape, distribution and color of the similar microstructures were compared. It was summarized identification methods to above several kinds of similar microstructure which are useful for the metallographic workers.
中图分类号 TG115.21+3
所属栏目 实践经验
基金项目
收稿日期 2011/12/14
修改稿日期
网络出版日期
作者单位点击查看
备注燕样样(1963-),女,高级实验师。
引用该论文: YAN Yang-yang. Analysis and Identification of Similar Microstructure of Steel[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2012, 48(6): 390～393
燕样样. 钢材相似显微组织的分析与鉴别[J]. 理化检验－物理分册, 2012, 48(6): 390～393
被引情况:
【1】王希,柏明清,周杨,唐春容,李建宏, "环戊烷进料线三通裂纹原因分析",理化检验－物理分册 51, 216-218(2015)
【2】韩志良, "调质组织中铁素体成因分析",理化检验－物理分册 51, 123-125(2015)
【3】燕样样,姚永红, "钢材相似显微组织的分析与鉴别(续)",理化检验－物理分册 49, 79-83(2013)
【4】金林奎,王春亮,赵建国, "齿轮渗碳淬火组织粗大原因分析及工艺改进",理化检验－物理分册 51, 259-262(2015)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】上海市机械制造工艺研究所. 金相分析技术[M]. 上海:上海科学技术文献出版社,1987:280.
【2】孙洪涛. 金相检验[M]. 北京: 中国计量出版社, 2010:115-117.
【3】任松赞,张静江,陈质如,等. 钢铁材料金相图谱[M]. 上海:上海科学技术文献出版社,2005:58,77.
【2】孙洪涛. 金相检验[M]. 北京: 中国计量出版社, 2010:115-117.
【3】任松赞,张静江,陈质如,等. 钢铁材料金相图谱[M]. 上海:上海科学技术文献出版社,2005:58,77.
相关信息