抗硫油管断裂原因分析
Reasons Analysis on Fracture of SSC Resistant Tubing
摘 要
采用化学成分分析、断口分析、金相检验、扫描电镜分析等方法, 对某油田抗硫油管的断裂原因进行了分析。结果表明: 油管在硫化氢的腐蚀作用下, 首先在管壁上产生局部腐蚀, 继而在应力的作用下产生微裂纹并扩展, 最终发生应力腐蚀断裂。最后, 通过实验室模拟井况条件试验, 提出了选择合适材料的建议。
硫化氢应力腐蚀
材料
SSC resistant
tubing
sulfide stress corrosion
material
Abstract
Fracture reason analysis was conducted to a SSC resistant tubing by means of chemical compositions analysis, fracture analysis, metallographic examination and scanning electron microscopy analysis. The results show that local corrosion in H2S environment occured on the pipe body, which made microcracks initiate and propagate, and stress corrosion cracking (SCC)take palce eventually. The corrosion experiments simulated the oil country medium were done in the lab, and suggestion of choosing appropriate material is proposed finally.
中图分类号 TG115.2
所属栏目 质量控制与失效分析
基金项目
收稿日期 2011/2/23
修改稿日期
网络出版日期
作者单位点击查看
备注郭金宝(1961-),男,工程师,学士。
引用该论文: GUO Jin-bao,GUO Yu-yi. Reasons Analysis on Fracture of SSC Resistant Tubing[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2012, 48(6): 403～406
郭金宝,郭毓奕. 抗硫油管断裂原因分析[J]. 理化检验－物理分册, 2012, 48(6): 403～406
被引情况:
【1】谢华,翟博,王瑞, "F304不锈钢阀门卸压杆断裂原因分析",理化检验－物理分册 51, 73-75(2015)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李兆敏, 王登庆,张志宏,等. 深井硫化氢腐蚀规律试验研究[J]. 石油钻采工艺, 2008,30(6):79-81.
【2】袁中华,叶顶鹏,李永刚,等. 钻杆接头断裂原因分析[J]. 理化检验-物理分册, 2009,45(7):455-457.
【3】王成达,严密林,赵伟新,等. 油气田开发中H2S/CO2腐蚀研究进展[J]. 西安石油大学学报, 2005,20(5): 66-70.
【4】白真权,李鹤林,刘道新,等. 模拟油田H2S/CO2环境中N80钢的腐蚀及影响因素研究[J]. 材料保护, 2003,36(4): 32-34.
【5】姜方,戴海黔,曹小燕,等. 油套管在H2S/CO2共存时的腐蚀机理研究[J]. 石油天然气化工, 2005,34(3): 213-215.
【2】袁中华,叶顶鹏,李永刚,等. 钻杆接头断裂原因分析[J]. 理化检验-物理分册, 2009,45(7):455-457.
【3】王成达,严密林,赵伟新,等. 油气田开发中H2S/CO2腐蚀研究进展[J]. 西安石油大学学报, 2005,20(5): 66-70.
【4】白真权,李鹤林,刘道新,等. 模拟油田H2S/CO2环境中N80钢的腐蚀及影响因素研究[J]. 材料保护, 2003,36(4): 32-34.
【5】姜方,戴海黔,曹小燕,等. 油套管在H2S/CO2共存时的腐蚀机理研究[J]. 石油天然气化工, 2005,34(3): 213-215.
相关信息