轴承齿圈开裂原因分析
Analysis on Cracking Reason of Bearing Gear Ring
摘 要
使用了约4 a(年)的轴承齿圈在服役过程中发生开裂。为查明其开裂的原因, 通过化学成分分析、力学性能测试、宏观及微观检验对轴承齿圈进行了分析。结果表明: 轴承齿圈开裂的原因是孔内壁表面腐蚀坑处产生微裂纹, 加之齿圈本身强度低于技术要求值, 在交变应力的作用下发生了疲劳断裂。
腐蚀
疲劳
bearing gear ring
corrosion
fatigue
Abstract
A bearing gear ring was broken after using about four years. By means of chemical composition analysis, mechanical property testing, macro and micro examination, the cracking reason of the bearing gear ring was analyzed. The results showed that the microcrack was formed at the etch pit of bolt hole inner surface, and the yield strength of gear ring was lower than specification, and the alternate stresses existed in the service process which caused the fatigue failure.
中图分类号 TH133.3
所属栏目 质量控制与失效分析
基金项目
收稿日期 2012/4/20
修改稿日期
网络出版日期
作者单位点击查看
备注王春亮(1978-), 男, 工程师, 硕士。
引用该论文: WANG Chun-liang,CHEN Hua-feng,SHA Fei. Analysis on Cracking Reason of Bearing Gear Ring[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2012, 48(7): 468～471
王春亮,陈华锋,沙菲. 轴承齿圈开裂原因分析[J]. 理化检验－物理分册, 2012, 48(7): 468～471
被引情况:
【1】李伟光,赵万祥,孔全兴,贾斌斌, "电动给水泵电机轴腐蚀失效分析",理化检验－物理分册 51, 442-444(2015)
【2】浦 红,刘 晶,方 政,王仲琨, "50Mn钢齿圈断齿原因分析",理化检验－物理分册 52, 499-502(2016)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】束德林.金属力学性能[M].北京:机械工业出版社,1999:128-142.
【2】机械工业理化检验人员技术培训和资格鉴定委员会.金相检验[M].上海:上海科学普及出版社,2006:259-262.
【2】机械工业理化检验人员技术培训和资格鉴定委员会.金相检验[M].上海:上海科学普及出版社,2006:259-262.
相关信息