Failure Analysis on Surface Pitting and Stripping of Cylindrical Mixer Rolling Ring
摘 要
通过宏观检查、磁粉检测、化学成分分析、硬度测试以及金相检验等方法对某圆筒混料机的滚圈进行分析, 找出了引起滚圈表面出现点蚀及剥离的主要原因。结果表明: 由于滚圈铸钢材料组织粗大, 且在后续热处理过程中由于方法不当产生了魏氏组织, 使得材料的力学性能较差, 从而导致其在使用过程中出现点蚀及剥离等失效现象。
Abstract
Through macro inspection, magnetic particle testing, chemical compositions analysis, hardness testing and metallographic examination, the surface pitting and stripping reasons of a cylindrical mixer rolling ring were analyzed. The results show that original microstructure of the rolling ring was too coarse and Widmanstatten formed in the subsequent heat treatment process, which reduced the mechanical properties of the material and resulted in the pitting and stripping failure in service process of the rolling ring.
中图分类号 TG142.1+1
所属栏目 质量控制与失效分析
基金项目
收稿日期 2011/11/18
修改稿日期
网络出版日期
作者单位点击查看
备注李志宏(1966-),女,正高级工程师。
引用该论文: LI Zhi-hong,LIU Liang,WU Jia-sheng,LI Peng. Failure Analysis on Surface Pitting and Stripping of Cylindrical Mixer Rolling Ring[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2012, 48(8): 555~556
李志宏,刘亮,武家升,李朋. 圆筒混料机滚圈表面点蚀及剥离失效分析[J]. 理化检验-物理分册, 2012, 48(8): 555~556
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王俊,王玉玲. 摆动凸轮失效分析[J]. 理化检验-物理分册, 2009,44(3): 179-180.
【2】赵连城. 金属热处理原理[M]. 哈尔滨: 哈尔滨工业大学出版社,1987.
【3】吴连生. 失效分析技术[M]. 重庆:四川科学技术出版社,1985.
【2】赵连城. 金属热处理原理[M]. 哈尔滨: 哈尔滨工业大学出版社,1987.
【3】吴连生. 失效分析技术[M]. 重庆:四川科学技术出版社,1985.
相关信息