高温过热器G102管内壁氧化皮剥落导致的爆管原因分析及对策
Cause Analysis and Countermeasures on Tube Bursting Caused by Peel-off of Scale of G102 Tube in High Temperature Superheater
摘 要
对高温过热器G102管的爆管原因进行了分析, 结果表明: G102管爆管是由于管子内壁偏厚的氧化皮剥落、在下弯头堆积, 造成管内通流面积减小而引起管子长时过热导致的。针对该问题, 对G102钢等铁素体钢管进行内壁氧化皮厚度测量及剥落风险评估, 可大大降低或避免由于氧化皮剥落、堆积引起的爆管事故。
爆管
铁素体钢
氧化皮测量
剥落风险评估
high temperature superheater
tube bursting
ferritic steel
scale measurement
peel-off risk assessment
Abstract
The tube bursting reason of the G102 tube of high temperature superheater was analyzed. The results showed that the tube bursting caused by long-term overheat, resulted from the thick scale of inner wall peeled, and deposited at the lower elbow of tube, and caused the flow area decrease. The tube bursting caused by peel-off and accumulation of scale was reduced greatly, or even avoided by measuring the scale thickness and peel-off risk assessment of ferritic steel tube.
中图分类号 TK228
所属栏目 质量控制与失效分析
基金项目
收稿日期 2011/10/12
修改稿日期
网络出版日期
作者单位点击查看
备注孟卫疆(1976-), 男, 工程师, 学士。
引用该论文: MENG Wei-jiang,YU Yue-jiang,ZHENG Fang-ping,CUI Xiong-hua. Cause Analysis and Countermeasures on Tube Bursting Caused by Peel-off of Scale of G102 Tube in High Temperature Superheater[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2012, 48(9): 613～617
孟卫疆,余跃江,郑坊平,崔雄华. 高温过热器G102管内壁氧化皮剥落导致的爆管原因分析及对策[J]. 理化检验－物理分册, 2012, 48(9): 613～617
被引情况:
【1】马元坤, "超超临界锅炉末级过热器T92钢管爆管原因分析",理化检验－物理分册 49, 834-837(2013)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】赵永宁,刘爽.102钢高温过热器管内壁氧化皮脱落研究[J].热加工工艺, 2010,39(22):203-206.
【2】胡新芳,刘蕊,付敏,等.102钢内壁氧化皮脱落原因分析[J].山东电力技术,2008(6):16-17.
【3】李耀君.氧化皮脱落导致的过热器管爆管分析[J].热力发电,2005(6): 56-59.
【4】郑世津.锅炉蒸汽侧氧化层剥落的治理[J].华东电力, 2003(12):66-68.
【5】DL/T 884-2004火电厂金相检验与评定技术导则[S].
【2】胡新芳,刘蕊,付敏,等.102钢内壁氧化皮脱落原因分析[J].山东电力技术,2008(6):16-17.
【3】李耀君.氧化皮脱落导致的过热器管爆管分析[J].热力发电,2005(6): 56-59.
【4】郑世津.锅炉蒸汽侧氧化层剥落的治理[J].华东电力, 2003(12):66-68.
【5】DL/T 884-2004火电厂金相检验与评定技术导则[S].
相关信息