QDH钢制凹模失效分析
Failure Analysis of Concave Mould Made of QDH Steel
摘 要
通过化学成分分析、宏观检验和金相检验等方法对QDH钢制凹模失效的原因进行了分析。结果表明: 由于脱碳层未完全去除, 渗氮件表面粗糙以及在渗氮层中形成了脉状及网状氮化物, 使模具的冲击韧度显著降低, 从而导致模具发生了早期开裂、塌陷及局部剥落。
凹模
脱碳层
脉状氮化物
QDH steel
concave mould
decarburizing layer
nervation nitride
Abstract
By means of chemical composition analysis, macro examination, metallographic examination and so on, the failure reason of QDH concave mould was analyzed. The results showed that decarburizing layer of the concave mould wasn′t removed absolutely, the surface of mould was coarse, nervation and wave nitride was came into being in the nitrided case. All of these made the mould impact toughness significantly reduced, leading to mould happened early cracking, collapse and local spalling.
中图分类号 TG162.41
所属栏目 质量控制与失效分析
基金项目
收稿日期 2011/11/30
修改稿日期
网络出版日期
作者单位点击查看
备注曾会书(1971-),男, 工程师。
引用该论文: ZENG Hui-shu,LI Wei. Failure Analysis of Concave Mould Made of QDH Steel[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2012, 48(9): 622～624
曾会书,李巍. QDH钢制凹模失效分析[J]. 理化检验－物理分册, 2012, 48(9): 622～624
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】GB/T 10561-2005钢中非金属夹杂物含量的测定标准评级图显微检验法[S].
【2】GB/T 11354-2005钢铁零件渗氮层深度测定和金相组织检验[S].
【3】马鹏飞, 李美兰.热处理技术[M]. 北京: 化学工业出版社, 2008:47.
【4】叶卫平, 张覃轶.热处理实用数据速查手册[M].北京: 机械工业出版社, 2005: 84.
【5】刘永铨.钢的热处理[M].北京: 冶金工业出版社, 1981:234.
【6】唐殿福, 卯石刚.钢的化学热处理[M].沈阳: 辽宁科学技术出版社, 2009: 423.
【7】魏兴钊, 朱伟恒, 朱繁康, 等. 4Cr5MoSiV1钢制热作模具若干失效形式与对策探讨[J].热处理技术与装备, 2009,30(3): 28.
【8】王荣滨.模具氮化十种缺陷分析与消除措施[J]. 模具制造, 2006(2): 60.
【9】郝清月.金属材料缺陷金相检测实例及缺陷金相图谱[M].北京: 中国知识出版社, 2006:377.
【2】GB/T 11354-2005钢铁零件渗氮层深度测定和金相组织检验[S].
【3】马鹏飞, 李美兰.热处理技术[M]. 北京: 化学工业出版社, 2008:47.
【4】叶卫平, 张覃轶.热处理实用数据速查手册[M].北京: 机械工业出版社, 2005: 84.
【5】刘永铨.钢的热处理[M].北京: 冶金工业出版社, 1981:234.
【6】唐殿福, 卯石刚.钢的化学热处理[M].沈阳: 辽宁科学技术出版社, 2009: 423.
【7】魏兴钊, 朱伟恒, 朱繁康, 等. 4Cr5MoSiV1钢制热作模具若干失效形式与对策探讨[J].热处理技术与装备, 2009,30(3): 28.
【8】王荣滨.模具氮化十种缺陷分析与消除措施[J]. 模具制造, 2006(2): 60.
【9】郝清月.金属材料缺陷金相检测实例及缺陷金相图谱[M].北京: 中国知识出版社, 2006:377.
相关信息