钻杆焊缝刺漏原因分析
Cause Analysis on Piercing of a Drilling Pipe at Welding Area
摘 要
通过刺孔形貌观察、扫描电镜分析、能谱分析、化学成分分析、金相检验以及硬度测试等方法, 对钻杆焊缝刺漏失效的原因进行了分析。结果表明: 失效钻杆在焊缝区域存在一定面积的焊接灰斑缺陷, 使得钻杆焊缝区的结合强度、疲劳强度以及冲击韧度大大降低, 从而导致了该次钻杆焊缝区的早期刺漏失效。最后根据钻杆失效的原因, 提出了相对应的改进措施和建议。
钻杆
刺漏
welding grey spot defect
drilling pipe
piercing
Abstract
The analysis of piercing hole macro-appearance, microstructure, energy spectrum, chemical compositions and hardness test were carried out to the piercing drilling pipe. The results show that as a certain area of welding grey spot defect existed in welding area of the drilling pipe, the bonding strength, fatigue property and impact toughness of the drilling pipe welding seam were reduced greatly, which led to the piercing of the drilling pipe early at welding area. Finally, the prevention methods and suggestion were put forward.
中图分类号 TE931
所属栏目 质量控制与失效分析
基金项目
收稿日期 2012/1/10
修改稿日期
网络出版日期
作者单位点击查看
备注余世杰(1982-), 男, 工程师, 博士研究生。
引用该论文: YU Shi-jie,YUAN Peng-bin,MA Jin-shan,JING Song-long,GONG Dan-mei. Cause Analysis on Piercing of a Drilling Pipe at Welding Area[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2012, 48(10): 693～696
余世杰,袁鹏斌,马金山,荆松龙,龚丹梅. 钻杆焊缝刺漏原因分析[J]. 理化检验－物理分册, 2012, 48(10): 693～696
被引情况:
【1】龚丹梅,余世杰,袁鹏斌,帅亚民, "水平井中S135钻杆断裂原因分析",理化检验－物理分册 51, 69-72(2015)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】陈大中,相克,郑方翎,等. 用电镜对焊接灰斑缺陷的性质和分类的研究[J]. 电子显微学报,1990(3):149.
【2】陈祥禧. 石油钻杆摩擦焊焊缝缺陷分析[J]. 石油机械,1993,21(10):16-21.
【3】API Spec 5DP-2009Specification for drill pipe[S].
【4】李鹤林,李平全,冯耀荣. 石油钻柱失效分析及预防[M] . 北京:石油工业出版社,1999.
【5】宋辉.摩擦焊在石油机械制造业中的应用[J]. 科技信息,2007(28):60.
【2】陈祥禧. 石油钻杆摩擦焊焊缝缺陷分析[J]. 石油机械,1993,21(10):16-21.
【3】API Spec 5DP-2009Specification for drill pipe[S].
【4】李鹤林,李平全,冯耀荣. 石油钻柱失效分析及预防[M] . 北京:石油工业出版社,1999.
【5】宋辉.摩擦焊在石油机械制造业中的应用[J]. 科技信息,2007(28):60.
相关信息