Cause Analysis and Countermeasures on Bursting of T91 Steel Tubes in Supercritical Boiler Final Superheater
摘 要
对某超临界锅炉末级过热器T91钢管的爆管原因进行了分析。结果表明: 该T91钢管爆管是由于管内壁偏厚的氧化皮剥落, 在下弯头处堆积造成管内介质流量减少,引起钢管过热所致。针对该问题, 通过对T91等铁素体锅炉钢管进行内壁氧化皮厚度测量, 并根据测量结果采取相应措施, 可大大减少或避免由于氧化皮剥落、堆积而引起的爆管事故。
Abstract
The bursting reason of T91 steel tube in supercritical boiler final superheater was analyzed. The results show that the steel tube bursting resulted from the thick oxide scale of inner wall peeled and deposited at the lower elbow of the tube, which caused the flow area in the tube decreasing and resulted in superheating. The number of bursting of T91 ferritic steel tubes caused by peel-off and accumulation of oxide scale could be decreased greatly or even avoided by measuring the oxide scale thickness and adopting corresponding measures according to the measure results.
中图分类号 TK228
所属栏目 质量控制与失效分析
基金项目
收稿日期 2012/1/31
修改稿日期
网络出版日期
作者单位点击查看
备注包文东(1975-), 男, 工程师, 学士。
引用该论文: BAO Weng-dong,ZHENG Fang-ping,CUI Xiong-hua,WANG Fei. Cause Analysis and Countermeasures on Bursting of T91 Steel Tubes in Supercritical Boiler Final Superheater[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2012, 48(10): 704~707
包文东,郑坊平,崔雄华,王飞. 超临界锅炉末级过热器T91钢管爆管原因分析及预防措施[J]. 理化检验-物理分册, 2012, 48(10): 704~707
被引情况:
【1】蒙新明,张路,赖云亭,於旻,张国栋, "某超临界机组锅炉过热器管爆管原因分析",理化检验-物理分册 51, 353-357(2015)
【2】张学星,谭晓霞,曾凡伟,陈明, "亚临界锅炉前墙吊挂管爆管原因分析",理化检验-物理分册 51, 270-273(2015)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】黄兴德,周新雅,游喆,等.超(超)临界锅炉高温受热面蒸汽氧化皮的生长与剥落特性[J]. 动力工程,2009,29(6):602-608.
【2】王殿仲,徐宪龙. 600 MW超临界锅炉高温受热面氧化皮形成与脱落原因分析及其改进措施[J]. 电力设备,2008,9(3):45-47.
【3】DL/T 884-2004火电厂金相检验与评定技术导则[S].
【4】DL/T 438-2009火力发电厂金属技术监督规程[S].
【2】王殿仲,徐宪龙. 600 MW超临界锅炉高温受热面氧化皮形成与脱落原因分析及其改进措施[J]. 电力设备,2008,9(3):45-47.
【3】DL/T 884-2004火电厂金相检验与评定技术导则[S].
【4】DL/T 438-2009火力发电厂金属技术监督规程[S].
相关信息