机械疲劳对40Cr钢显微组织的影响
Influence of Mechanical Fatigue on Microstructure of 40Cr Steel
摘 要
以汽车曲轴常用材料40Cr钢为研究对象, 用透射电镜对经过不同疲劳周次的试样进行显微组织观察, 研究其显微组织与机械疲劳的对应关系。研究表明: 在同一应力水平下, 随着疲劳循环次数的增加, 位错从晶界出发向晶内扩展, 位错的形态由无规律的分布到形成位错条带, 最后形成亚晶粒组织。机械疲劳循环次数与位错密度的函数关系为ρ=2.88×108 N+5.271 2×108。
机械疲劳
显微组织
位错密度
40Cr steel
mechanical fatigue
microstructure
dislocation density
Abstract
40Cr steel was researched as the common material used for automobile crankshaft.TEM was usedto observe the change of microstructure, and to find the relationship between the change of microstructure andmechanical fatigue.The research results showed that, in the same stress level, with the fatigue cycle numberincreased, the dislocations in the 40Cr initiated from the grain boundaries, extended into the grain.And themorphology of the dislocation became to sub grains from bands.The dislocation density increasing caused bymechanical fatigue had liner relationship with fatigue cycle number.The relationship was: ρ=2.88×108 N +5.271 2×108.
中图分类号 TG113.12
所属栏目 试验与研究
基金项目 国家质检总局科研项目(2011IK043)
收稿日期 2012/6/26
修改稿日期
网络出版日期
作者单位点击查看
备注吴益文(1967-), 男, 高级工程师, 硕士。
引用该论文: WU Yi-wen,REN Chen,HUA Yi,XU Ling-yun,WANG Hong-bin,ZHANG Cong. Influence of Mechanical Fatigue on Microstructure of 40Cr Steel[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2012, 48(11): 709～712
吴益文,任晨,华沂,徐凌云,汪宏斌,张聪. 机械疲劳对40Cr钢显微组织的影响[J]. 理化检验－物理分册, 2012, 48(11): 709～712
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李伟.GCr15钢超高周疲劳行为的研究 [D].成都: 西南交通大学, 2004.
【2】吴益文, 华沂, 蒋海宁, 等.汽车发动机缸体的再制造问题研究[J].检验检疫学刊, 2009, 19(6): 35-37.
【3】杨晓华, 兑卫真.回火温度对40Cr钢疲劳裂纹扩展的影响[J].机电技术, 2003, 26(9): 229-234.
【4】张聪.再制造技术产品的物理检验鉴别技术研究[D].上海: 上海大学, 2010.
【5】AMINUDIN B A, JAE-EUNG OH, JUNG YOONLEE.Analysis of an in-line engine crankshaft underthefiring condition[J].Journal of Automobile Engi-neering, 2005, 219(3): 345-353.
【6】GB 3075—2008 金属材料疲劳试验轴向力控制方法[S].
【7】梁秀兵, 陈永雄.自动化电弧高速喷涂技术再制造发动机曲轴[J].中国表面工程, 2010(23): 112-116.
【8】HIRSCH P, HOWIE A, NICHOLSON R, et al.Electron Microscopy of Thin Crystals[M].Florida: Krieger Publishing Company, 1977.
【9】LORETTO MH.Electron Beam Analysis of Materials[M].Florida: Chapman and Hall, 1994.
【10】PESICKA J, KUZEL R, DRONHOFER A, et al.The evolution of dislocation density during heat treat-ment and creep of tempered martensite ferritic steels[J].Acta Materialia, 2003(51): 4847-4862.
【11】胡赓祥, 蔡珣, 戎永华.材料科学基础[M].上海: 上海交通大学出版社, 2006: 99-100.
【12】弗里埃德尔J.位错[M].王煜, 译.北京: 科学出版社, 1984: 27-28.
【2】吴益文, 华沂, 蒋海宁, 等.汽车发动机缸体的再制造问题研究[J].检验检疫学刊, 2009, 19(6): 35-37.
【3】杨晓华, 兑卫真.回火温度对40Cr钢疲劳裂纹扩展的影响[J].机电技术, 2003, 26(9): 229-234.
【4】张聪.再制造技术产品的物理检验鉴别技术研究[D].上海: 上海大学, 2010.
【5】AMINUDIN B A, JAE-EUNG OH, JUNG YOONLEE.Analysis of an in-line engine crankshaft underthefiring condition[J].Journal of Automobile Engi-neering, 2005, 219(3): 345-353.
【6】GB 3075—2008 金属材料疲劳试验轴向力控制方法[S].
【7】梁秀兵, 陈永雄.自动化电弧高速喷涂技术再制造发动机曲轴[J].中国表面工程, 2010(23): 112-116.
【8】HIRSCH P, HOWIE A, NICHOLSON R, et al.Electron Microscopy of Thin Crystals[M].Florida: Krieger Publishing Company, 1977.
【9】LORETTO MH.Electron Beam Analysis of Materials[M].Florida: Chapman and Hall, 1994.
【10】PESICKA J, KUZEL R, DRONHOFER A, et al.The evolution of dislocation density during heat treat-ment and creep of tempered martensite ferritic steels[J].Acta Materialia, 2003(51): 4847-4862.
【11】胡赓祥, 蔡珣, 戎永华.材料科学基础[M].上海: 上海交通大学出版社, 2006: 99-100.
【12】弗里埃德尔J.位错[M].王煜, 译.北京: 科学出版社, 1984: 27-28.
相关信息