45钢热处理组织异常原因分析与控制
Reason Analysis and Control of Abnormal Heat Treatment Structures of 45 Steel
摘 要
45钢在使用过程中热处理组织出现晶粒粗大、淬透性差的问题。经检验发现多个炉次生产的产品均出现了此问题, 因此分析认定这是一个系统的质量缺陷问题, 钢水中杂质含量较多且分布不均匀、轧制温度较高是造成该问题的主要原因, 并对此提出了解决的方案与方法。
晶粒粗大
淬透性
过烧
轧制工艺
45 steel
coarse grain
hardenability
overheat
rolling technology
Abstract
The coarse grain and low hardenability in heat treatment of 45steel have appeared in use.Inspections showed that such problems were found in several furnace products, so it was a systemic quality defect.The main reasons were more impurities and non-distributions, high rolling temperature, then effective solutions andmethods were presented.
中图分类号 TG157
所属栏目 质量控制与失效分析
基金项目
收稿日期 2012/6/25
修改稿日期
网络出版日期
作者单位点击查看
备注卢爱凤(1975-), 女, 工程师。
引用该论文: LU Ai-feng. Reason Analysis and Control of Abnormal Heat Treatment Structures of 45 Steel[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2012, 48(11): 766～769
卢爱凤. 45钢热处理组织异常原因分析与控制[J]. 理化检验－物理分册, 2012, 48(11): 766～769
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】朱苗勇.现代冶金学[M]. 北京: 冶金工业出版社, 2004.
【2】国际钢铁协会. 洁净钢———洁净钢生产工艺技术[M].中国金属学会, 译. 北京: 冶金工业出版社, 2009.
【3】董瀚.先进钢铁材料[M].北京: 科学出版社, 2008.
【4】黄新民.材料研究方法[M].哈尔滨: 哈尔滨工业大学出版社, 2008.
【2】国际钢铁协会. 洁净钢———洁净钢生产工艺技术[M].中国金属学会, 译. 北京: 冶金工业出版社, 2009.
【3】董瀚.先进钢铁材料[M].北京: 科学出版社, 2008.
【4】黄新民.材料研究方法[M].哈尔滨: 哈尔滨工业大学出版社, 2008.
相关信息