42CrMo轴件断裂原因分析
Analysis on Fracture Reason of 42CrMo Axis
摘 要
利用宏观检验、金相检验、有效硬化层硬度测试及扫描电镜观察等方法对某42CrMo轴件的断裂原因进行了分析。结果表明: 该轴件的断裂属性为脆性断裂, 而轴件材料存在的晶粒粗大、魏氏体脆性相、网状铁素体以及晶界上存在的屈氏体等组织缺陷是造成早期脆性断裂的主要原因。
脆性断裂
魏氏体
有效硬化层
axis
brittle fracture
widmanstatten structure
effective hardening layer
Abstract
The fracture reason of a 42CrMo axis was analyzed by means of macroscopic examination, metallographic examination, the effective depth testing of hardening layer, SEM observation and so on. The results showed that the fracture attribute of axis was brittle fracture, and the early brittle fracture was caused by the microstructure defect which was found in the axis material, such as coarse grain, brittle phase of widmanstatten structure, reticulate ferrite, as well as the troostite existed on grain boundaries and so on.
中图分类号 TG162.71 TG157
所属栏目 质量控制与失效分析
基金项目
收稿日期 2011/11/30
修改稿日期
网络出版日期
作者单位点击查看
备注祁学军(1978-), 男, 助理工程师, 硕士。
引用该论文: QI Xue-jun,YANG Dong-mei,YAN Gao-hua. Analysis on Fracture Reason of 42CrMo Axis[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2013, 49(1): 55～58
祁学军,杨冬梅,晏高华. 42CrMo轴件断裂原因分析[J]. 理化检验－物理分册, 2013, 49(1): 55～58
被引情况:
【1】王硕,徐世斌, "42CrMo钢导向端轴的断裂原因分析",理化检验－物理分册 51, 814-816(2015)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】傅国如, 张峥.失效分析技术[J].理化检验-物理分册, 2005, 41(4): 318-323.
【2】陈国华, 陈灵杰.新氢压缩机排气阀盖断裂失效分析[J].理化检验-物理分册, 2011, 47(10): 649-652.
【2】陈国华, 陈灵杰.新氢压缩机排气阀盖断裂失效分析[J].理化检验-物理分册, 2011, 47(10): 649-652.
相关信息