Analysis on Leakage Reason of WP304WX Pipe
摘 要
不锈钢管道使用5 a(年)后出现泄漏事故。采用化学成分分析、硬度测试、金相检验、晶间腐蚀与断口扫描电镜分析方法, 对泄漏原因进行了分析。结果表明: 焊接过程中造成的贫铬及残余应力的存在导致了管道的开裂。建议对管道所有焊缝热影响区进行探伤, 查找腐蚀裂纹, 对发现的裂纹进行打磨和补焊处理, 并进行消除残余应力处理。
Abstract
The pipe leaked in use after five years. The leakage reason of the pipe was analyzed by means of chemical composition analysis, hardness testing, metallographic examination, intergranular corrosion analysis and fracture SEM analysis. The results showed that chromium depletion in heat-affected zone during the welding process and the residual stress led to the pipeline cracking. It was suggested that all of the welding seam should be inspected nondestructively to find corrosion cracks, and the cracks should be grinded and repaired by welding processing, and the residual stress should be eliminated.
中图分类号 TG457.6
所属栏目 质量控制与失效分析
基金项目
收稿日期 2012/3/9
修改稿日期
网络出版日期
作者单位点击查看
备注丁二喜(1982-),男,工程师,工学硕士。
引用该论文: DING Er-xi,WU Ji-quan,ZHANG Ju-guang,QIU Kang-yong. Analysis on Leakage Reason of WP304WX Pipe[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2013, 49(1): 68~70
丁二喜,吴继权,张居光,邱康勇. WP304WX管道泄漏原因分析[J]. 理化检验-物理分册, 2013, 49(1): 68~70
被引情况:
【1】王希,柏明清,周杨,唐春容,李建宏, "环戊烷进料线三通裂纹原因分析",理化检验-物理分册 51, 216-218(2015)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】胡世炎. 破断故障金相分析[M]. 北京: 国防工业出版社, 1979: 280-282.
【2】上海交通大学. 金属断口分析[M]. 北京: 国防工业出版社, 1979: 210-214.
【3】张栋, 钟培道. 失效分析[M]. 北京: 国防工业出版社, 2005: 198-206.
【4】吴连生. 失效分析技术及其应用-第二讲 断裂分类及韧、脆断裂的转变[J]. 理化检验-物理分册, 1995, 31(6): 57-61.
【2】上海交通大学. 金属断口分析[M]. 北京: 国防工业出版社, 1979: 210-214.
【3】张栋, 钟培道. 失效分析[M]. 北京: 国防工业出版社, 2005: 198-206.
【4】吴连生. 失效分析技术及其应用-第二讲 断裂分类及韧、脆断裂的转变[J]. 理化检验-物理分册, 1995, 31(6): 57-61.
相关信息