3Cr20Ni11Mo2PB钢气阀断裂原因分析
Causes Analysis on Fracture of 3Cr20Ni11Mo2PB Steel Gas Valves
摘 要
通过对3Cr20Ni11Mo2PB钢原材料及断裂气阀的力学性能、硬度、断口及显微组织进行分析, 对气阀批量脆性断裂的原因进行了分析。结果表明: 气阀脆性断裂主要是由于气阀加工过程中固溶处理温度过高, 使其显微组织严重过热局部过烧, 极大降低了材料的塑性和韧性导致的。
气阀
固溶温度
过热
过烧
3Cr20Ni11Mo2PB steel
gas valve
solution temperature
over-heat
over-burn
Abstract
The batch brittle fracture causes of 3Cr20Ni11Mo2PB steel gas valves were analyzed by means of mechanical properties test, hardness test, metallographic examination and fracture analysis. The result show that the brittle fracture of the gas valves was mainly caused by the serious over-heated and partial over-burnt structure, which greatly reduced the plasticity and toughness of the gas valves because of the high solution temperature.
中图分类号 TG142.73
所属栏目 质量控制与失效分析
基金项目
收稿日期 2012/4/25
修改稿日期
网络出版日期
作者单位点击查看
备注张全新(1976-),男,高级工程师。
引用该论文: ZHANG Quan-xin. Causes Analysis on Fracture of 3Cr20Ni11Mo2PB Steel Gas Valves[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2013, 49(2): 127～129
张全新. 3Cr20Ni11Mo2PB钢气阀断裂原因分析[J]. 理化检验－物理分册, 2013, 49(2): 127～129
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】丁文华,张绪江,陈玉章. 不锈钢的热处理[M]. 北京:机械工业出版社,1983.
【2】中国机械工程学会理化检验分会. 金相检验[M]. 上海: 上海材料研究所理化检验编辑部, 1983.
【3】庄东汉. 材料失效分析[M]. 上海: 华东理工大学出版社, 2009.
【2】中国机械工程学会理化检验分会. 金相检验[M]. 上海: 上海材料研究所理化检验编辑部, 1983.
【3】庄东汉. 材料失效分析[M]. 上海: 华东理工大学出版社, 2009.
相关信息