Q235B钢原油储罐消防喷淋管线开裂原因分析
Reasons Analysis on Fracture of Q235B Steel Fire Spray Pipeline on Crude Oil Tank
摘 要
通过宏观观察、化学成分分析、力学性能测试、金相检验、扫描电镜观察以及能谱分析等方法对某Q235B钢原油储罐消防喷淋管线多处频繁开裂的原因进行了分析。结果表明: 该消防喷淋管线焊缝一侧存在较多层状分布的硅酸盐类非金属夹杂物是导致其层状开裂的根本原因。
层状开裂
非金属夹杂物
fire spray pipeline
lamellar cracking
non-metallic inclusion
Abstract
The frequent cracking reasons of Q235B steel fire spray pipeline on crude oil tank were analyzed through macroscopic observation, mechanical properties test, metallographic examination, scanning electron microscopy observation and energy spectrum analysis. The results show that the main reason for lamellar cracking of the fire spray pipeline was the large numbers of silicate non-metallic inclusions which distributed in the form of layers beside the weld.
中图分类号 TE821
所属栏目 质量控制与失效分析
基金项目
收稿日期 2012/4/7
修改稿日期
网络出版日期
作者单位点击查看
备注韩燕(1981-),女,工程师。
引用该论文: HAN Yan,LI Jin-feng,ZHAO Xue-hui,QU Ting-ting. Reasons Analysis on Fracture of Q235B Steel Fire Spray Pipeline on Crude Oil Tank[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2013, 49(2): 133～137
韩燕,李金凤,赵雪会,瞿婷婷. Q235B钢原油储罐消防喷淋管线开裂原因分析[J]. 理化检验－物理分册, 2013, 49(2): 133～137
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】赵帜. 大型可燃液体储罐的消防喷淋冷却系统设计[J]. 石油化工设计,2007,24(4):4-6.
【2】GB/T 3091-2001低压流体输送用焊接钢管[S].
【3】胡世炎. 机械失效分析手册[M]. 成都:四川科学技术出版社,1989:258-259.
【4】茹春生,张俊伟. Q235B钢板冷弯开裂原因分析及预防措施[J]. 山西冶金,2011,34(5):47-49.
【5】张德堂,李淑媛,夏慧琴. 钢中非金属夹杂物对疲劳性能的影响[J]. 航空材料,1982,2(2):54-59.
【6】田白玉. 钢中非金属夹杂物及其金相鉴别[J]. 机械产品与科技,2004(4):31-34.
【2】GB/T 3091-2001低压流体输送用焊接钢管[S].
【3】胡世炎. 机械失效分析手册[M]. 成都:四川科学技术出版社,1989:258-259.
【4】茹春生,张俊伟. Q235B钢板冷弯开裂原因分析及预防措施[J]. 山西冶金,2011,34(5):47-49.
【5】张德堂,李淑媛,夏慧琴. 钢中非金属夹杂物对疲劳性能的影响[J]. 航空材料,1982,2(2):54-59.
【6】田白玉. 钢中非金属夹杂物及其金相鉴别[J]. 机械产品与科技,2004(4):31-34.
相关信息