油、套管脱扣、挤毁和破裂失效分析
Failure Analysis Including Pulling out, Collapse and Fracture of Tubing and Casing
摘 要
通过调查研究和失效分析, 列举了我国油田常见的油、套管脱扣、挤毁、破裂等失效形式, 给出了每种失效形式的定义, 对每种油、套管失效形式产生的原因及其影响因素进行了分析, 并提出了具体预防措施。
套管
脱扣
挤毁
破裂
失效分析
tubing
casing
pulling out
collapse
fracture
failure analysis
Abstract
The failure modes of pulling out, collapse, fracture and etc. of tubing and casing were enumerated on the basis of investigation and failure analysis, the definitions for every failure mode were presented, the failure causes and influence factors were analyzed, and the detailed prevent measures were brought forward.
中图分类号 TE92
所属栏目 综述
基金项目
收稿日期 2012/3/19
修改稿日期
网络出版日期
作者单位点击查看
备注高林(1957-),男,工程师。口井报废。
引用该论文: GAO Lin,LV Shuan-lu,LI He-lin,LUO Fa-qian,ZHOU Jie,YANG Cheng-xin,LI Ning,QIN Hong-de,LE Fa-guo,LIU De-ying. Failure Analysis Including Pulling out, Collapse and Fracture of Tubing and Casing[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2013, 49(3): 177～181
高林,吕拴录,李鹤林,骆发前,周杰,杨成新,李宁,秦宏德,乐法国,刘德英. 油、套管脱扣、挤毁和破裂失效分析[J]. 理化检验－物理分册, 2013, 49(3): 177～181
被引情况:
【1】张钧,赵国仙,吕祥鸿,宋文文, "塔里木油田某井油管脱落原因分析",理化检验－物理分册 50, 845-848(2014)
【2】谢俊峰,宋文文,常泽亮,吕拴录,文志明,吴云才,秦德友, "某天然气井13Cr油管腐蚀原因",腐蚀与防护 35, 754-757(2014)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】吕拴录, 韩勇. 特殊螺纹接头油、套管使用及展望[J]. 石油工业技术监督,2003(3):1-4.
【2】吕拴录, 李鹤林, 骆发前, 等. 油、套管粘扣和泄漏失效分析综述[J]. 石油矿场机械, 2010, 39(4):21-25.
【3】吕拴录. φ139.7 mm×7.72 mm J55长圆螺纹套管脱扣原因分析[J]. 钻采工艺, 2005, 28(2): 73-77.
【4】吕拴录,宋治. J值在API圆螺纹连接中含义初探[J]. 石油钻采工艺,1995(5): 56-62.
【5】API SPEC 5BSpecification for Threading,Gaging,and Threaded Inspection of Casing,Tubing,and Line Pipe Threads[S]. 15th ed. Washington (DC):API,2004.
【6】API SPEC 5CTSpecification for Casing and Tubing[S]. 7th ed. Washington(DC):API,2001.
【7】API RP 5C1Recommended Practice for Care and Use of Casing and Tubing[S]. 18th ed. Washington DC:API,1999.
【8】袁鹏斌,吕拴录,姜涛,等. 长圆螺纹套管脱扣原因分析[J]. 石油矿场机械, 2007(10): 68-72.
【9】LU Shuan-lu,HAN Yong,QIN Chang-yi,et al. Analysis of well casing connection pullout[J]. Engineering Failure Analysis,2006,13(4): 638-645.
【10】LU Shuan-lu,LI Zhi-hou,HAN Yong,et al. High dogleg severity, wear ruptures casing string[J]. Oil and Gas, 2000,98(12):49.
【11】吕拴录,李鹤林. V150套管接箍破裂原因分析[J]. 理化检验-物理分册,2005,41(z1): 285-290.
【12】吕拴录. 73.0 mm×5.51 mm J55平式油管断裂和弯曲原因分析[J]. 石油矿场机械, 2007,36(8): 47-49.
【13】LU Shuan-lu,ZHAO Ke-feng. H2O2 well cleanout leads to explosion[J]. Oil and Gas,2004(11):44-47.
【2】吕拴录, 李鹤林, 骆发前, 等. 油、套管粘扣和泄漏失效分析综述[J]. 石油矿场机械, 2010, 39(4):21-25.
【3】吕拴录. φ139.7 mm×7.72 mm J55长圆螺纹套管脱扣原因分析[J]. 钻采工艺, 2005, 28(2): 73-77.
【4】吕拴录,宋治. J值在API圆螺纹连接中含义初探[J]. 石油钻采工艺,1995(5): 56-62.
【5】API SPEC 5BSpecification for Threading,Gaging,and Threaded Inspection of Casing,Tubing,and Line Pipe Threads[S]. 15th ed. Washington (DC):API,2004.
【6】API SPEC 5CTSpecification for Casing and Tubing[S]. 7th ed. Washington(DC):API,2001.
【7】API RP 5C1Recommended Practice for Care and Use of Casing and Tubing[S]. 18th ed. Washington DC:API,1999.
【8】袁鹏斌,吕拴录,姜涛,等. 长圆螺纹套管脱扣原因分析[J]. 石油矿场机械, 2007(10): 68-72.
【9】LU Shuan-lu,HAN Yong,QIN Chang-yi,et al. Analysis of well casing connection pullout[J]. Engineering Failure Analysis,2006,13(4): 638-645.
【10】LU Shuan-lu,LI Zhi-hou,HAN Yong,et al. High dogleg severity, wear ruptures casing string[J]. Oil and Gas, 2000,98(12):49.
【11】吕拴录,李鹤林. V150套管接箍破裂原因分析[J]. 理化检验-物理分册,2005,41(z1): 285-290.
【12】吕拴录. 73.0 mm×5.51 mm J55平式油管断裂和弯曲原因分析[J]. 石油矿场机械, 2007,36(8): 47-49.
【13】LU Shuan-lu,ZHAO Ke-feng. H2O2 well cleanout leads to explosion[J]. Oil and Gas,2004(11):44-47.
相关信息