Analysis on Confirmation of the Changed Methods of Tensile Test for Metallic Materials at Room Temperature
摘 要
通过对低合金钢标准拉伸试样在不同加载条件下的拉伸试验, 分析了控制方式和加载速率对材料力学性能的影响, 并结合金属材料室温拉伸试验方法, 详细论述了检测标准变更后实验室应采取的措施, 以及对新标准重新确认的方法、步骤和应注意的问题, 以证实实验室有相应的能力继续满足试验标准的要求。
Abstract
By means of the tensile tests of standard tensile samples of low alloy steel under different loading conditions, the influence of control mode and loading rate on mechanical properties of materials was analyzed. And in order to confirm that the laboratory has the ability to continue to meet the requirements of the test standard, combining with tensile test methods for metallic materials at room temperature, it was discussed in detail including the measures should be taken by the laboratory after the testing standards were changed, as well as to the reconfirmed methods, procedures and problems should be paid attention to.
中图分类号 TG115.5+2
所属栏目 实验室认可
基金项目
收稿日期 2012/12/10
修改稿日期
网络出版日期
作者单位点击查看
备注张万松(1964-), 男, 副教授, 理学博士。
引用该论文: ZHANG Wan-song,WANG Jian-guo. Analysis on Confirmation of the Changed Methods of Tensile Test for Metallic Materials at Room Temperature[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2013, 49(5): 310~313
张万松,王建国. 浅析金属材料室温拉伸试验方法变更后的证实[J]. 理化检验-物理分册, 2013, 49(5): 310~313
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】陈华锋, 王滨, 黄旭东.拉伸试验的速率探讨[J].理化检验-物理分册,2009, 45(5):285-287.
【2】李和平.拉伸、冲击和硬度试验方法国际标准的修订和问题[J].理化检验-物理分册,2010, 46(6):369-373.
【3】董强,宰绍峰,孙建林,等.GB/T 228.1-2010中的拉伸试验速率及其控制[J].理化检验-物理分册,2011, 47(12): 774-781.
【4】岑风,陈益华,张珂.金属材料室温拉伸试验新旧国家标准的对比分析[J].理化检验-物理分册, 2012, 48(12): 804-810.
【5】王开远.浅析新版金属材料室温拉伸试验方法国家标准[J].大众标准化, 2012(12): 66-69.
【2】李和平.拉伸、冲击和硬度试验方法国际标准的修订和问题[J].理化检验-物理分册,2010, 46(6):369-373.
【3】董强,宰绍峰,孙建林,等.GB/T 228.1-2010中的拉伸试验速率及其控制[J].理化检验-物理分册,2011, 47(12): 774-781.
【4】岑风,陈益华,张珂.金属材料室温拉伸试验新旧国家标准的对比分析[J].理化检验-物理分册, 2012, 48(12): 804-810.
【5】王开远.浅析新版金属材料室温拉伸试验方法国家标准[J].大众标准化, 2012(12): 66-69.
相关信息