Causes Analysis on Surface Defects of HRB400 Rebars
摘 要
某厂生产的HRB400螺纹钢表面出现了大量的结疤和类似于“裂纹”的缺陷,通过宏观分析、化学成分分析、金相检验以及能谱分析等方法对螺纹钢表面缺陷产生的原因进行了分析。结果表明: 螺纹钢表面的缺陷是由于轧制原因而造成的结疤和折叠类缺陷; 另由于终轧温度较高和冷却速率较快而在螺纹钢表面形成了贝氏体组织, 这也是螺纹钢生产所不允许的。
Abstract
A large number of scar and similar ‘crack’ defects were found on surface of HRB400 rebar, and the causes of the surface defects were analyzed by means of macroscopic analysis, chemical compositions analysis, metallographic examination and energy spectrum analysis. The results show that the surface defects of HRB400 rebar were fold and scar which caused by improper rolling. In addition, too high final rolling temperature and fast cooling rate resulted in formation of bainite at surface layer of the rebar, and this was also not allowed during the rebar production.
中图分类号 TG335.6+4
所属栏目 质量控制与失效分析
基金项目
收稿日期 2012/11/11
修改稿日期
网络出版日期
作者单位点击查看
备注李雪峰(1972-),男,高级工程师,学士。
引用该论文: LI Xue-feng,WANG Chun-fen,GUO Hai-xia. Causes Analysis on Surface Defects of HRB400 Rebars[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2013, 49(6): 413~415
李雪峰,王春芬,郭海霞. HRB400螺纹钢表面缺陷形成原因分析[J]. 理化检验-物理分册, 2013, 49(6): 413~415
被引情况:
【1】肖卫强,刘丹敏,王少博,张隐奇,吉 元,徐学东, "HRB500热轧带肋钢筋断后伸长率偏低原因分析",理化检验-物理分册 52, 284-286(2016)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】GB1499.2-2007钢筋混凝土用钢 第2部分: 热轧带肋钢筋[S].
【2】袁威, 鲁雄刚, 郭曙强, 等. 20MnSi螺纹钢夹杂物产生的原因[J]. 上海大学学报:自然科学版,2004,10(5): 471-474.
【3】米国瑞, 李文学. 20MnSi螺纹钢裂纹产生原因研究[J]. 包头钢铁学院学报,1997,16(1): 42-45.
【4】王子亮, 王新江, 赵自义, 等. 螺纹钢生产工艺与技术[M]. 北京:冶金工业出版社,2008:238-239.
【5】李智博,常金丽,张贺宗. 螺纹钢脆断分析[J]. 理化检验-物理分册,2005,41(10): 521-523.
【2】袁威, 鲁雄刚, 郭曙强, 等. 20MnSi螺纹钢夹杂物产生的原因[J]. 上海大学学报:自然科学版,2004,10(5): 471-474.
【3】米国瑞, 李文学. 20MnSi螺纹钢裂纹产生原因研究[J]. 包头钢铁学院学报,1997,16(1): 42-45.
【4】王子亮, 王新江, 赵自义, 等. 螺纹钢生产工艺与技术[M]. 北京:冶金工业出版社,2008:238-239.
【5】李智博,常金丽,张贺宗. 螺纹钢脆断分析[J]. 理化检验-物理分册,2005,41(10): 521-523.
相关信息