12.9级内六角圆柱螺栓断裂失效分析
Failure Analysis on Fracture of Grade 12.9 Hexagon Socket Head Cap Screws
摘 要
某40CrMo钢12.9级高强度内六角圆柱螺栓在使用过程中发生断裂，使用光电直读光谱仪、光学显微镜和扫描电子显微镜对断裂螺栓的化学成分、显微组织以及断口形貌等进行了分析。结果表明: 该螺栓断裂为因与酸性介质接触导致氢渗入而引起的氢脆断裂。
断裂
氢脆
screw
fracture
hydrogen embrittlement
Abstract
The grade 12.9 hexagon socket head cap screws made of 40CrMo steel fractured in use. chemical compositions, microstructure, fracture morphology of the screws were analyzed by photoelectric direct reading spectrometer, optical microscope and SEM. The results show that the fracture of the screws was hydrogen embrittlement fracture caused by the hydrogen penetration from the acidic medium.
中图分类号 TG111.91
所属栏目 质量控制与失效分析
基金项目
收稿日期 2012/12/4
修改稿日期
网络出版日期
作者单位点击查看
备注蒋佩华(1977-),女,工程师,硕士。
引用该论文: JIANG Pei-hua,WANG Wei,WANG Hui,XU Zong-fan. Failure Analysis on Fracture of Grade 12.9 Hexagon Socket Head Cap Screws[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2013, 49(8): 560～562
蒋佩华,王蔚,王慧,许宗凡. 12.9级内六角圆柱螺栓断裂失效分析[J]. 理化检验－物理分册, 2013, 49(8): 560～562
被引情况:
【1】金林奎,邓永玖,赵建国,王春亮, "20CrNi3H钢汽车后桥主动齿轮的工艺改进",理化检验－物理分册 51, 342-345(2015)
【2】骆 亍,宾远红,李培芬, "1018钢螺钉断裂失效分析",理化检验－物理分册 52, 281-283(2016)
【3】王挺,李振华, "镀锌螺钉断裂分析",理化检验－物理分册 51, 668-670(2015)
【4】钟奇鸣,李翔, "减震胶套壳体的断裂原因分析",理化检验－物理分册 52, 825-827(2016)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】周崎,陈明,曹标. 弹性垫圈断裂原因分析[J]. 物理测试,2006,25(2):52-54.
【2】王运知,王育妮. 航空发动机用轻型弹簧垫圈断裂故障分析及改进方案[J]. 现代机械,2010(4):48-50.
【2】王运知,王育妮. 航空发动机用轻型弹簧垫圈断裂故障分析及改进方案[J]. 现代机械,2010(4):48-50.
相关信息