Residual Stress Measurement for Cast TC4 Alloy by Electron Beam Welding
摘 要
对铸造TC4钛合金进行电子束焊接, 使用X射线衍射法对焊后母材、热影响区以及焊缝的表面残余应力分布状况进行测试和分析。结果表明: 垂直于焊缝方向的测试点上, 焊缝及热影响区在横、纵两个方向上主要存在拉应力; 剪切应力数值均在±50 MPa范围内, 可以认为对焊缝性能没有影响。沿焊缝长度方向的测试点上, 无论横向应力还是纵向应力, 焊缝起始端的应力值要低于焊缝终止端的应力值。纵向残余应力表现为拉应力, 横向残余应力由压应力逐渐向拉应力方向转变。
Abstract
Cast TC4 alloy were welded by electron beam welding, and residual stress in matrix, heat affect zone and joint was tested by X-ray diffraction method. The results showed that there were tensile stress in joint and heat affect zone in transverse direction and longitudinal direction, where testing points were perpendicular to welding line, the shear stress values were in the scale of ±50 MPa, which had no effect on mechanical property of the joint. Testing point along the welding line, whether transverse or longitudinal stress, stress in start of welding joint was lower than which in the end of welding joint. Longitudinal stress was tensile stress, and transverse compress stress change to tensile stress gradually.
中图分类号 TG407 TG115.22+2.2
所属栏目 试验与研究
基金项目
收稿日期 2013/1/30
修改稿日期
网络出版日期
作者单位点击查看
备注陆业航(1967-), 女, 高级工程师, 学士。
引用该论文: LU Ye-hang,ZHANG Jie,WU Bing,LI Zhong-cheng. Residual Stress Measurement for Cast TC4 Alloy by Electron Beam Welding[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2013, 49(11): 711~713
陆业航,张杰,吴冰,李众城. 铸造TC4钛合金电子束焊残余应力测试[J]. 理化检验-物理分册, 2013, 49(11): 711~713
被引情况:
【1】刘延辉,瞿伟成,朱小刚,王联凤,李崇桂,孙靖,程灵钰,于治水,郭立杰, "激光3D打印TC4钛合金工件根部裂纹成因分析",理化检验-物理分册 52, 682-685(2016)
【2】蔡联瑜,孔纲,翁天宇,江爱华,齐凯,王新华, "6.8级冷镦螺栓的表层残余应力分布",理化检验-物理分册 52, 99-103(2016)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】赵锡龙, 宋旭, 张建勋. TC4钛合金激光焊接接头力学行为的原位研究[J].中国有色金属学报, 2012,22(2):388-393.
【2】要玉宏,刘江南,马丽,等.铸造TC4钛合金细节疲劳强度DFRcutoff的研究[J].稀有金属材料与工程, 2009,38(9):1530-1532.
【3】雷文光,于兰兰,毛小南,等.电子束冷床熔炼TC4钛合金铸锭凝固过程有限元模拟[J].铸造, 2010,59(9):912-916.
【4】宫平.影响TC4钛合金电子束焊焊缝形状因素的研究[D].大连: 大连交通大学,2008.
【5】李晓延,巩水利,关桥.大厚度钛合金结构电子束焊接制造基础研究[J].焊接学报,2010,31(2):107-112.
【6】吴冰,张建勋,巩水利,等.厚板钛合金电子束焊接残余应力分布特征[J].焊接学报,2010,31(2):10-12.
【7】郑卜祥,宋永伦,席峰,等.对接焊铝合金板材残余应力的X射线测试[J].机械工程学报,2009,45(3):275-280.
【8】张定铨, 何家文. 材料中残余应力的X射线衍射分析和作用[M].西安: 西安交通大学出版社, 1999.
【9】BS EN 15305-2008Non-destructive Testing-Test Method for Residual Stress Analysis by X-ray Diffraction[S].
【10】付鹏飞,黄锐,刘方军,等.TA12钛合金电子束焊接组织性能及残余应力分析[J].焊接学报, 2007,28(2):82-84.
【2】要玉宏,刘江南,马丽,等.铸造TC4钛合金细节疲劳强度DFRcutoff的研究[J].稀有金属材料与工程, 2009,38(9):1530-1532.
【3】雷文光,于兰兰,毛小南,等.电子束冷床熔炼TC4钛合金铸锭凝固过程有限元模拟[J].铸造, 2010,59(9):912-916.
【4】宫平.影响TC4钛合金电子束焊焊缝形状因素的研究[D].大连: 大连交通大学,2008.
【5】李晓延,巩水利,关桥.大厚度钛合金结构电子束焊接制造基础研究[J].焊接学报,2010,31(2):107-112.
【6】吴冰,张建勋,巩水利,等.厚板钛合金电子束焊接残余应力分布特征[J].焊接学报,2010,31(2):10-12.
【7】郑卜祥,宋永伦,席峰,等.对接焊铝合金板材残余应力的X射线测试[J].机械工程学报,2009,45(3):275-280.
【8】张定铨, 何家文. 材料中残余应力的X射线衍射分析和作用[M].西安: 西安交通大学出版社, 1999.
【9】BS EN 15305-2008Non-destructive Testing-Test Method for Residual Stress Analysis by X-ray Diffraction[S].
【10】付鹏飞,黄锐,刘方军,等.TA12钛合金电子束焊接组织性能及残余应力分析[J].焊接学报, 2007,28(2):82-84.
相关信息