60Si2CrVA弹簧断裂原因分析
Analysis on Fracture Reason of 60Si2CrVA Spring
摘 要
通过断口分析、金相检验、硬度测试及化学成分分析等方法, 对60Si2CrVA弹簧进行断裂原因分析。结果表明: 该弹簧断裂失效性质为疲劳断裂; 弹簧端圈磨削裂纹是导致弹簧断裂的根本原因; 提出了防止磨削裂纹产生的建议, 对指导生产有一定参考价值。
疲劳断裂
磨削裂纹
spring
fatigue fracture
grinding cracks
Abstract
In order to analyze the fracture reason of 60Si2CrVA spring, the analysis such as fracture appearance, microstructure, hardness and chemical compositions were conducted. The results indicated that the fracture of spring was fatigue, it′s prime reason was grinding cracks on the end of the springrests. The prevention measures of grinding cracks on springs, which exhibited the special value for guiding the production, have been proposed.
中图分类号 TH135
所属栏目 质量控制与失效分析
基金项目
收稿日期 2013/1/28
修改稿日期
网络出版日期
作者单位点击查看
备注侯珍(1985-), 女, 工程师, 硕士。
引用该论文: HOU Zhen,GONG Xin-yong,ZHENG Qiu-yue. Analysis on Fracture Reason of 60Si2CrVA Spring[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2013, 49(11): 777～780
侯珍,宫心勇,郑秋越. 60Si2CrVA弹簧断裂原因分析[J]. 理化检验－物理分册, 2013, 49(11): 777～780
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】上海交通大学《金属断口分析》编写组.金属断口分析[M].北京: 国防工业出版社,1979:51-55.
【2】张建军.磨削裂纹的产生与防治措施[J].煤矿机械,2002,32(8):37-38.
【3】上海市金属学会.金属材料缺陷金相图谱[M].上海: 上海科学技术出版社,1966:228-229.
【4】张纹.磨削加工中产生裂纹的原因与防止措施[J].农业装备技术,2008,34(2):58-59.
【5】王力,王培科.60Si2Mn弹簧挡圈断裂原因分析及防治措施[J].煤矿机械,2011,32(11):125-126.
【2】张建军.磨削裂纹的产生与防治措施[J].煤矿机械,2002,32(8):37-38.
【3】上海市金属学会.金属材料缺陷金相图谱[M].上海: 上海科学技术出版社,1966:228-229.
【4】张纹.磨削加工中产生裂纹的原因与防止措施[J].农业装备技术,2008,34(2):58-59.
【5】王力,王培科.60Si2Mn弹簧挡圈断裂原因分析及防治措施[J].煤矿机械,2011,32(11):125-126.
相关信息