Failure Analysis on Internal Corrosion of Crude Oil Pipeline
摘 要
对某站原油外输管线的内腐蚀穿孔管段进行了取样分析,使用光学显微镜、X射线衍射仪、能谱分析仪等设备对管子腐蚀形貌进行观察,发现腐蚀产物中有不同类型的羟基氧化铁以及FeCO3和FeS等,分析了导致管子电化学腐蚀穿孔的主要原因,对杂散电流和氯离子加速腐蚀穿孔的机制进行了深入的探讨,并对该类腐蚀防护提出了建议。
Abstract
The internal corrosion pipe specimens cut from the crude oil pipeline were analyzed by using theoptical microscope,X-ray diffraction analyzer and SEM energy spectrum analyzer.It was found that there existeddifferent types of hydroxy iron oxide as well as FeCO3and FeS in the corrosion products.The main causes of theelectrochemical corrosion perforation were discussed,and then the accelerated effect of stray electric current andchloride ion on the corrosion perforation mechanism was proposed,and further the protection methods against thiskind of corrosion were put forward.
中图分类号 TG142
所属栏目 质量控制与失效分析
基金项目
收稿日期 2013/2/19
修改稿日期
网络出版日期
作者单位点击查看
备注田嘉治(1993-),男,学士。
引用该论文: TIAN Jia-zhi,LV Qing-gang,YANG Dong-ming,TIAN Qing-chao. Failure Analysis on Internal Corrosion of Crude Oil Pipeline[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2013, 49(12): 843~847
田嘉治,吕庆钢,羊东明,田青超. 集输管内腐蚀失效原因分析[J]. 理化检验-物理分册, 2013, 49(12): 843~847
被引情况:
【1】周波,朱建雷,李宁,张国正,杨成新,程春杰, "P110油管腐蚀穿孔原因分析",理化检验-物理分册 52, 335-338(2016)
【2】聂向晖,王高峰,丰振军,许彦,刘迎来, "X60M钢管泄漏原因分析",理化检验-物理分册 52, 811-814(2016)
【3】伍超群,刘英坤,熊文, "燃气钢管腐蚀穿孔原因分析",理化检验-物理分册 50, 137-139(2014)
【4】赵向杰,王温栋, "某输气管线穿孔原因分析",理化检验-物理分册 52, 584-588(2016)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】熊慧欣,周立祥.不同晶型羟基氧化铁(FeOOH)的形成及其在吸附去除Cr(Ⅵ)上的作用[J]. 岩石矿物学杂志,2008,27(6):559-566.
【2】董晓明,田青超.S135钻杆失效分析[J]. 理化检验-物理分册,2007,43(9):476-479.
【3】王俊,齐文元,周卫国.高压输电线路对埋地输油管道中杂散电流的影响[J]. 全面腐蚀控制,2010,24(7):48-52.
【4】俞蓉蓉.地下金属管道的腐蚀与防护[M]. 北京:石油工业出版社,1998.
【5】胡士信.阴极保护手册[M]. 北京:化学工业出版社, 1999.
【2】董晓明,田青超.S135钻杆失效分析[J]. 理化检验-物理分册,2007,43(9):476-479.
【3】王俊,齐文元,周卫国.高压输电线路对埋地输油管道中杂散电流的影响[J]. 全面腐蚀控制,2010,24(7):48-52.
【4】俞蓉蓉.地下金属管道的腐蚀与防护[M]. 北京:石油工业出版社,1998.
【5】胡士信.阴极保护手册[M]. 北京:化学工业出版社, 1999.
相关信息