集箱管接座角焊缝缺陷浅析及返修处理
Brief Analysis and Repair Methods of the Pipe Connection Seat Fillet Weld Defect
摘 要
屏式过热器出口集箱管接座角焊缝缺陷的存在严重影响锅炉正常安全运行。通过渗透检测，发现集箱管接座的焊接裂纹是由根部未熔合扩展到表面引起的。根部未熔合的产生是由于焊接前对口时坡口间隙过小以及焊接时未采用氩弧焊封底。提出了具体的返修处理方案。
应力集中
根部未熔合
冷裂纹
返修
T/P91 material
Stress concentration
Root incomplete fusion
Cold crack
Repair
Abstract
The pipe connection seat fillet welds defect of superheater outlet collector existing seriously affected the normal safety operation. The paper used PT method and found that the welding crack of the pipe connection seat was caused by the expansion from root incomplete fusion to surface. Root incomplete fusion was due to aligning small gaps of groove before welding and not adoping argon arc welding bottom. This paper presented the detailed repair measures.
中图分类号 TG115.28
所属栏目 实践经验
基金项目
收稿日期 2010/7/16
修改稿日期
网络出版日期
作者单位点击查看
备注章丽虎(1986-)，男，助理工程师，工学学士，主要从事电站建设无损检测工作。
引用该论文: ZHANG Li-Hu,DONG Ji-Yuan. Brief Analysis and Repair Methods of the Pipe Connection Seat Fillet Weld Defect[J]. Nondestructive Testing, 2011, 33(6): 52～53
章丽虎,董吉原. 集箱管接座角焊缝缺陷浅析及返修处理[J]. 无损检测, 2011, 33(6): 52～53
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李志翔，李晓平，赵永强.火力发电厂新材料T91/P91钢性能综述［J］.云南电力技术,2004(3):15-17.
【2】郑中甫，陈泉.工艺参数及焊接材料对T91/P91钢焊缝性能的影响［J］.热加工工艺,2006(5):41-43.
【2】郑中甫，陈泉.工艺参数及焊接材料对T91/P91钢焊缝性能的影响［J］.热加工工艺,2006(5):41-43.
相关信息