FGH96、FGH97粉末盘的无损检测
NDT Method for the FGH96 and FGH97 Superalloy Powder Disks
摘 要
通过对FGH96粉末、FGH97粉末镍基高温合金涡轮盘、篦齿盘无损检测方法研究，确定了粉末盘超声检测和荧光检测工艺。通过检测结果研究发现，热等静压+锻造态合金有利于超声检测，并发现了缺陷显示;直接成型热等静压态合金有利于荧光检测，并发现了缺陷显示。
超声波检测
荧光检测
Powder disk
Ultrasonic inspection
Fluorescent inspection
Abstract
Through the studying of NDT methods used for FGH96 and FGH97 powder Nickel-based superalloy turbine disk and labyrinth disk, the ultrasonic inspection and fluorescent particle inspection processes have been determined for the powder disks. The inspection results prove that the alloy made by hot isostatic pressing(HIP)+forging is more suitable for exposing indications with ultrasonic inspection, while the alloy made by direct HIP is good for indicating flaws with fluorescent particle inspection.
中图分类号 TG115.28
所属栏目 实践经验
基金项目
收稿日期 2011/5/4
修改稿日期
网络出版日期
作者单位点击查看
备注董德秀(1969-)，女，高级工程师，主要从事航空产品的无损检测工程应用。
引用该论文: DONG De-Xiu,XIONG Ying,LIU Huai-Nan,ZHANG Chuan-Ming. NDT Method for the FGH96 and FGH97 Superalloy Powder Disks[J]. Nondestructive Testing, 2012, 34(5): 76～80
董德秀,熊瑛,刘怀南,张传明. FGH96、FGH97粉末盘的无损检测[J]. 无损检测, 2012, 34(5): 76～80
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张凤戈，张义文，陶宇.镍基粉末高温合金的超声无损检测［J］.粉末冶金,2004,14(3):16-19.
【2】国为民，吴剑涛，张凤戈，等.粉末高温合金中夹杂物特性及不同成型工艺的关系［J］.材料导报,2004,18(11):87-91.
【3】Paul Mclntire.美国无损检测手册［M］.上海：世界图书出版公司,1996.
【2】国为民，吴剑涛，张凤戈，等.粉末高温合金中夹杂物特性及不同成型工艺的关系［J］.材料导报,2004,18(11):87-91.
【3】Paul Mclntire.美国无损检测手册［M］.上海：世界图书出版公司,1996.
相关信息