大型GCr15锻件超声波检测密集型缺陷的成因
The Cause of Cluster of UT Indications of GCr15 Heavy Steel Forgings
摘 要
在超声波检测大型GCr15锻件(冶炼路径：EAF-LF-VD-铸锭-热送-锻造;首次生产锻比6∶1，改锻锻比为5∶1，直径 650 mm)过程中，探出纵向的超声波密集型缺陷。对其定位解剖，且用金相、扫描电镜和能谱分析等方法进行分析。结果表明：大型轴承钢锻材中心区域存在严重的碳偏析是导致GCr15锻件出现超声波的衰减与反射的原因。
成分偏析
超声波检测
反射
吸收
碳化物
GCr15 forging
Composition segregation
Ultrasonic inspection
Reflection
Absorb
Carbide
Abstract
Means such as Macroetch Testing and Micrographic examination, SEM and XPS were used to analyze the cluster of UT indications of GCr15 Heavy steel Forgings (press rate: 4∶1, 650 mm). The results showed that the main cause of the cluster of indications was many segregated spots of(Fe3C，α-Fe) structure. The spots were herein defined as cluster of UT indications in the forgings.
中图分类号 TG115.28
所属栏目 试验研究
基金项目
收稿日期 2011/12/3
修改稿日期
网络出版日期
作者单位点击查看
备注赵荒培(1985-)，男，学士，主要从事无损检测工作。
引用该论文: ZHAO Huang-Pei,DANG Zheng-Hui,CHEN Ping,CONG Tie-Sheng. The Cause of Cluster of UT Indications of GCr15 Heavy Steel Forgings[J]. Nondestructive Testing, 2012, 34(12): 77～80
赵荒培,党政辉,陈平,丛铁声. 大型GCr15锻件超声波检测密集型缺陷的成因[J]. 无损检测, 2012, 34(12): 77～80
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】孙海燕.大型锻件内部缺陷的预防与修复研究［C］//首届中国大型铸锻件制造技术发展论坛文集.沈阳：［出版者不详］,2006.
【2】赵晗，宫延声，沈晶渊，等.无标X射线衍射定量相分析的极小范数解［J］.金属学报.1990,26(6):452-456.
【3】赵晗，翁韶华.金相试样的预处理［J］.理化检验-物理分册,2005,41(9):480-484.
【4】姜晓霞.金相侵蚀过程的研究［J］.理化检验-物理分册,1987,26(4):26-33.
【5】李兆劲.大型轴类锻件产生小当量超声波探伤密集缺陷的原因及改善途径［J］.大型铸锻件,2001,1(1):37-39.
【6】汤宝华.高碳铬轴承钢网状碳化物的研究［D］.沈阳：东北大学,2006.
【2】赵晗，宫延声，沈晶渊，等.无标X射线衍射定量相分析的极小范数解［J］.金属学报.1990,26(6):452-456.
【3】赵晗，翁韶华.金相试样的预处理［J］.理化检验-物理分册,2005,41(9):480-484.
【4】姜晓霞.金相侵蚀过程的研究［J］.理化检验-物理分册,1987,26(4):26-33.
【5】李兆劲.大型轴类锻件产生小当量超声波探伤密集缺陷的原因及改善途径［J］.大型铸锻件,2001,1(1):37-39.
【6】汤宝华.高碳铬轴承钢网状碳化物的研究［D］.沈阳：东北大学,2006.
相关信息