Specific Surface Area Determination of Alumina Powders with Low Specific Surface Area by Gas Adsorption Method
摘 要
采用气体吸附法原理,以低比表面积氧化铝粉体标准物质为例,利用美国麦克仪器公司的ASAP2020比表面积和孔隙度分析仪测定其比表面积,通过改变测试条件分析各项参数值对测定结果的影响.结果表明:吸附系统“死体积”、样品用量和脱气条件等对测定结果都有比较明显的影响;对于低比表面积氧化铝粉体的理想测定条件为脱附温度250 ℃,脱附时间2 h,样品用量2.5~3 g.试验所得结果可为低比表面积粉体的比表面积准确测定提供参考.
Abstract
Using the gas adsorption method,the specific surface area of standard alumina powders was determined on ASAP2020 specific surface area and porosity analyzer made in Micromeritics Instrument Corporation of USA.And influencing factors on the specific surface area test results were studied.The results show that the adsorption system dead volume,sample amount and degas conditions all had obvious effects on the testing results,and the ideal testing condition for alumina powders with low specific surface area was that 2.5-3 g sample was desorbed at 250 ℃ for 2 h.This study could provide a reference for the low specific surface area determination.
中图分类号 O647 TB383
所属栏目 试验技术与方法
基金项目
收稿日期 2014/3/25
修改稿日期
网络出版日期
作者单位点击查看
备注王敏(1980-),女,工程师,硕士.
引用该论文: WANG Min. Specific Surface Area Determination of Alumina Powders with Low Specific Surface Area by Gas Adsorption Method[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2015, 51(2): 120~122
王敏. 气体吸附法测定低比表面积氧化铝粉体的比表面积[J]. 理化检验-物理分册, 2015, 51(2): 120~122
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】SHARMA A,RANI A,SINGH A,et al.Synthesis of alumina powder by the urea-glycine-nitrate combustion process:A mixed fuel approach to nanoscale metal oxides[J].Applied Nanoscience,2014,4(3):315-323.
【2】LEE D B,CHOI M J,PARK S,et al.Effect of Al2O3 nano-filler on properties of glass-based seals for solid oxide fuel cells[J].Journal of Nanoscience and Nanotechnology,2013,13:628-631.
【3】YU P C,CHEN C I,YANG R J,et al.Porous χ-Al2O3 flake powder as dye-fixing materials for inkjet printing paper[J].Journal of the American Ceramic Society,2012,95(7):2124-2126.
【4】李荣柱.氧化铝物理性能测定方法技术现状[J].理化检验-物理分册,2011,47(10):619-622,643.
【5】陈维平,韩孟岩,杨少锋.Al2O3陶瓷复合材料的研究进展[J].材料工程,2011(3):91-96.
【6】GOGOLEWSKI P,KLIMKE J,KRELL A,et al.Al2O3 tools towards effective machining of wood-based materials[J].Journal of Materials Processing Techno-logy,2009,209(5):2231-2236.
【7】李宏林,万新军,高晓宝,等.氧化铝粉末改性研究进展[J].中国陶瓷,2008,44(8):10-12.
【8】王鸿雁.α-Al2O3在耐火材料中应用性能的研究[J].有色设备,2007(3):31-33.
【9】GHANIZADEH S,BAO X,VAIDHYANATHAN B,et al.Synthesis of nano α-alumina powders using hydrothermal and precipitation routes:A comparative study[J].Ceramics International,2014,40(1):1311-1319.
【10】李波.α-氧化铝的X射线定量分析[J].理化检验-物理分册,2008,44(2):79-81,110.
【11】闫晓英,贺蒙.气体吸附BET法测量固态物质比表面积不确定度评定[J].现代测量与实验室管理,2008(3):20-22.
【12】李正明,杨云,郭增强.测定钴粉比表面积实验条件的探索[J].理化检验-物理分册,2004,40(11):564-565.
【13】彭人勇,周萍华,王廷吉,等.BET氮气吸附法测粉体比表面积误差探讨[J].非金属矿,2001,24(1):7-8.
【14】刘希尧.工业催化剂分析测试表征[M].北京:烃加工出版社,1990:44-55.
【15】GB/T 19587-2004气体吸附BET法测定固态物质比表面积[S].
【2】LEE D B,CHOI M J,PARK S,et al.Effect of Al2O3 nano-filler on properties of glass-based seals for solid oxide fuel cells[J].Journal of Nanoscience and Nanotechnology,2013,13:628-631.
【3】YU P C,CHEN C I,YANG R J,et al.Porous χ-Al2O3 flake powder as dye-fixing materials for inkjet printing paper[J].Journal of the American Ceramic Society,2012,95(7):2124-2126.
【4】李荣柱.氧化铝物理性能测定方法技术现状[J].理化检验-物理分册,2011,47(10):619-622,643.
【5】陈维平,韩孟岩,杨少锋.Al2O3陶瓷复合材料的研究进展[J].材料工程,2011(3):91-96.
【6】GOGOLEWSKI P,KLIMKE J,KRELL A,et al.Al2O3 tools towards effective machining of wood-based materials[J].Journal of Materials Processing Techno-logy,2009,209(5):2231-2236.
【7】李宏林,万新军,高晓宝,等.氧化铝粉末改性研究进展[J].中国陶瓷,2008,44(8):10-12.
【8】王鸿雁.α-Al2O3在耐火材料中应用性能的研究[J].有色设备,2007(3):31-33.
【9】GHANIZADEH S,BAO X,VAIDHYANATHAN B,et al.Synthesis of nano α-alumina powders using hydrothermal and precipitation routes:A comparative study[J].Ceramics International,2014,40(1):1311-1319.
【10】李波.α-氧化铝的X射线定量分析[J].理化检验-物理分册,2008,44(2):79-81,110.
【11】闫晓英,贺蒙.气体吸附BET法测量固态物质比表面积不确定度评定[J].现代测量与实验室管理,2008(3):20-22.
【12】李正明,杨云,郭增强.测定钴粉比表面积实验条件的探索[J].理化检验-物理分册,2004,40(11):564-565.
【13】彭人勇,周萍华,王廷吉,等.BET氮气吸附法测粉体比表面积误差探讨[J].非金属矿,2001,24(1):7-8.
【14】刘希尧.工业催化剂分析测试表征[M].北京:烃加工出版社,1990:44-55.
【15】GB/T 19587-2004气体吸附BET法测定固态物质比表面积[S].
相关信息