海上平台栈桥输油管线腐蚀失效原因
Corrosion Failure Reason of Transport Pipeline on Offshore Platform
摘 要
某海上平台栈桥输油管线在投产不到2 a时间内即发生局部腐蚀泄漏,泄漏部位处于管道底部焊缝连接位置.为了研究其腐蚀原因及对今后腐蚀控制提供参考,对发生腐蚀泄漏部位进行材质理化检验、腐蚀部位宏观形貌及SEM观察、能谱分析、腐蚀产物X射线衍射分析及电化学分析.结果表明,CO2腐蚀是造成该输油管线泄漏的原因,而导致焊接处优先发生泄漏的主要原因是焊缝和母材材质不匹配及焊接工艺不当引起焊缝自腐蚀电位低以及沟槽敏感性高.
输油管线
CO2腐蚀
自腐蚀电位
沟槽腐蚀
offshore platform
transport pipeline
CO2 corrosion
self corrosion potential
grooving corrosion
Abstract
Serious damage occurred on offshore platform pipeline in the production only after its service for only 2 years,the leak position was found in the pipe weld connections at the bottom of the pipe.The failed pipe was analyzed by means of chemical and mechanical properties tests,microstructure examination,XRD and energy-dispersive spectroscopy (EDS) to find out the corrosion and leakage reasons.The results showed that the reason of the pipeline corrosion was CO2 corrosion.The priority leakage reasons of welding were improper welding seam and high sensitivity of groove.
中图分类号 TG172
所属栏目 石油管道防腐蚀
基金项目
收稿日期 2013/4/9
修改稿日期
网络出版日期
作者单位点击查看
备注马晓勇(1986-),助理工程师,硕士,从事油田腐蚀管理工作
引用该论文: MA Xiao-yong,YANG Ming,LONG Yun,ZHAO Da-wei,CHEN Chao,YANG Hao-jie. Corrosion Failure Reason of Transport Pipeline on Offshore Platform[J]. Corrosion & Protection, 2015, 36(3): 230
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】陈圣乾,赵大伟,张炜强,等.某油田井口输油管线焊缝腐蚀失效分析[J].腐蚀与防护,2012,33(10):920-923.
【2】赵国仙,吕祥鸿,韩勇.某井油管腐蚀原因分析[J].材料工程,2010,3:51-55.
【3】方可伟,白荣国,刘晓军,等.核岛容器地脚螺栓的失效分析[J].腐蚀与防护,2012,33(12):1123-1126.
【4】刘东,艾俊哲,郭兴蓬.二氧化碳环境中碳钢电偶腐蚀行为研究[J].天然气工业,2007,28(10):11-13.
【5】WANG W,QI H B,LIU C S,et al.Methods of assessing the grooving corrosion of high frequency electric resistance welded pipe[J].Baosteel Technical Research,2010,4(3):27-31.
【6】HEUER J K,STUBBINS J F.An XPS characterization of FeCO3 films from CO2 corrosion[J].Corrosion Science,1999,41:1231-1243.
【7】毕宗岳,井晓天,鲜林云,等.热处理对连续油管焊缝沟槽腐蚀行为的影响[J].材料热处理技术,2011,40(8):150-153.
【2】赵国仙,吕祥鸿,韩勇.某井油管腐蚀原因分析[J].材料工程,2010,3:51-55.
【3】方可伟,白荣国,刘晓军,等.核岛容器地脚螺栓的失效分析[J].腐蚀与防护,2012,33(12):1123-1126.
【4】刘东,艾俊哲,郭兴蓬.二氧化碳环境中碳钢电偶腐蚀行为研究[J].天然气工业,2007,28(10):11-13.
【5】WANG W,QI H B,LIU C S,et al.Methods of assessing the grooving corrosion of high frequency electric resistance welded pipe[J].Baosteel Technical Research,2010,4(3):27-31.
【6】HEUER J K,STUBBINS J F.An XPS characterization of FeCO3 films from CO2 corrosion[J].Corrosion Science,1999,41:1231-1243.
【7】毕宗岳,井晓天,鲜林云,等.热处理对连续油管焊缝沟槽腐蚀行为的影响[J].材料热处理技术,2011,40(8):150-153.
相关信息