Corrosion and Electrochemical Behavior of A508III Low Alloy Steel in Boric Acid Solutions with Different Concentrations
摘 要
采用失重试验以及电化学测试研究了A508III低合金钢在25 ℃下0.05~0.5 mol/L硼酸溶液中的腐蚀与电化学行为.A508III钢在高浓度硼酸溶液中开路电位低于-500 mV(SCE),对应低电化学阻抗和高腐蚀速率.A508III钢在低浓度硼酸溶液中的开路电位会出现三种状况:低于-500 mV、大于-200 mV和介于其间的中间电位,其中高开路电位对应高电化学阻抗,而低开路电位对应低电化学阻抗.A508III钢在所测试的几种硼酸溶液中的阳极极化曲线与阴极极化曲线均在较宽的电位范围内表现出电位-电流线性关系,与溶液的低电导率有关.开路电位值以及相应的腐蚀速率结果与电位-pH图计算结果一致.
Abstract
The corrosion and electrochemical behavior of A508III low alloy steel in 0.05-0.5 mol/L H3BO3 solutions at 25 ℃ were studied by weight loss measurements and electrochemical measurements.Low open circuit potentials,low electrochemical impedance and high corrosion rates were observed in boric acid solutions of higher concentrations.Three levels of open circuit potentials,i.e.higher potentials (>-200 mV(SCE)),lower potentials (<-500 mV(SCE)),and intermediate potentials were observed in boric acid solutions of lower concentrations,where lower open circuit potentials corresponded to lower electrochemical impedance and higher open circuit potentials corresponded to higher electrochemical impedance.Anodic and cathodic polarization curves showed a linear relationship in a wide range of potential,which was related to the low conductivity of test solutions.The measured values of open circuit potentials,corrosion rates and the calculated E-pH diagrams were consistent.
中图分类号 TG174
所属栏目 试验研究
基金项目 上海市浦江人才计划(12PJ1403600);教育部博士点基金博导类项目(20123108110021);上海大学创新基金项目资助
收稿日期 2014/4/20
修改稿日期
网络出版日期
作者单位点击查看
联系人作者吕战鹏(zplu@shu.edu.cn)
备注吕战鹏(1967-),研究员,博士,从事材料腐蚀与防护研究.
引用该论文: XIAO Qian,Lv Zhan-peng,CHEN Jun-jie,XIA Xiao-feng,ZHOU Bang-xin. Corrosion and Electrochemical Behavior of A508III Low Alloy Steel in Boric Acid Solutions with Different Concentrations[J]. Corrosion & Protection, 2015, 36(3): 294
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】NRC IE Information Notice No.82-02,Degradation of threaded fasteners in the reactor coolant pressure boundary of PWR plants[R].US NRC,1982.
【2】KOOW H.Threaded-fastener experience in nuclear power plants[R].NUREG-0943,USNRC,1982.
【3】O′NEIL S,HALL J F.Boric acid corrosion of carbon and low alloy steel pressure boundary components in PWRs[R].EPRI Report NP-5985,EPRI,Palo Alto,CA:1988.
【4】CZAJKOWSKIC J.Survey of boric acid corrosion of carbon steel components in nuclear plants[R].NUREG/CR-5576,USNRC,1990.
【5】HALLJ F.A survey of the literature on low alloy steel fastener corrosion in PWR power plants[R].EPRI Report NP-3784,EPRI,Palo Alto,CA:1984.
【6】李承亮,张明乾.压水堆核电站反应堆压力容器材料概述[J].材料导报,2008,22(9):65-68.
【7】Boric Acid Corrosion Evaluation (BACE) Program Phase l-Task 1 Report[R].EPRI,Palo Alto,CA,1993.
【8】Boric Acid Corrosion Guidebook.Revision 1[R].EPRI,Palo Alto,CA:2001,No.1000975.
【9】PARK J H,CHOPRA O K,NATESAN K.Boric acid corrosion of light water reactor pressure vessel materials[R].NUREG/CR-6875,USNRC,2004,ANL-04/08.
【10】吴双成.硼酸的酸性问题探讨[J].电镀与环保,2012,32(1):52-54.
【11】宋立姝,周晓鸥.水溶液中硼酸的酸式离解及其强化问题[J].安庆师范学院学报,2001,7(2):80-82.
【12】石建敏,雷家荣,张玲,等.Al-B4C复合材料腐蚀行为研究[J].原子能科学技术,2010,44:159-165.
【13】魏宝明.金属腐蚀理论及应用[M].北京:化学工业出版社,1984:26-30.
【14】杨熙珍,杨武.金属腐蚀电化学热力学电位-pH图及其应用[M].北京:化学工业出版社,1991:100-105.
【2】KOOW H.Threaded-fastener experience in nuclear power plants[R].NUREG-0943,USNRC,1982.
【3】O′NEIL S,HALL J F.Boric acid corrosion of carbon and low alloy steel pressure boundary components in PWRs[R].EPRI Report NP-5985,EPRI,Palo Alto,CA:1988.
【4】CZAJKOWSKIC J.Survey of boric acid corrosion of carbon steel components in nuclear plants[R].NUREG/CR-5576,USNRC,1990.
【5】HALLJ F.A survey of the literature on low alloy steel fastener corrosion in PWR power plants[R].EPRI Report NP-3784,EPRI,Palo Alto,CA:1984.
【6】李承亮,张明乾.压水堆核电站反应堆压力容器材料概述[J].材料导报,2008,22(9):65-68.
【7】Boric Acid Corrosion Evaluation (BACE) Program Phase l-Task 1 Report[R].EPRI,Palo Alto,CA,1993.
【8】Boric Acid Corrosion Guidebook.Revision 1[R].EPRI,Palo Alto,CA:2001,No.1000975.
【9】PARK J H,CHOPRA O K,NATESAN K.Boric acid corrosion of light water reactor pressure vessel materials[R].NUREG/CR-6875,USNRC,2004,ANL-04/08.
【10】吴双成.硼酸的酸性问题探讨[J].电镀与环保,2012,32(1):52-54.
【11】宋立姝,周晓鸥.水溶液中硼酸的酸式离解及其强化问题[J].安庆师范学院学报,2001,7(2):80-82.
【12】石建敏,雷家荣,张玲,等.Al-B4C复合材料腐蚀行为研究[J].原子能科学技术,2010,44:159-165.
【13】魏宝明.金属腐蚀理论及应用[M].北京:化学工业出版社,1984:26-30.
【14】杨熙珍,杨武.金属腐蚀电化学热力学电位-pH图及其应用[M].北京:化学工业出版社,1991:100-105.
相关信息