风机叶片缺陷的无损检测方法比较与评价
Comparison and Evaluation on the Non-destructive Testing Methods for the Wind Turbine Blades Defects
摘 要
以文献调研的形式对风机叶片的典型缺陷及产生原因进行了分析与总结,叶片在生产、安装和运行的过程中,都有可能产生缺陷和损伤,通过检测与监测相结合的方式,可以预防并且能够避免意外事故的发生.目前,国内还没有相对完善的方案针对风机叶片的缺陷及损伤检测,结合风电产业的发展和对无损检测方法的比较与评价,得出以下结论:超声波检测技术适用于叶片安装前的静态检测,红外热成像检测技术比较适用于叶片的现场检测,声发射检测技术比较适用于叶片服役过程的动态监测.
缺陷
检测与监测
比较与评价
Wind turbine blade
Defect
Test and monitoring
Comparison and evaluation
Abstract
The paper analyzes and summarizes typical defects causes of wind turbine blade by the literature research.In the process of production,installation and operation,it is possible to produce defects and damage.The occurrence of the accident can be prevented and avoided through a combination of test and monitoring.At present,there is a lack of relatively perfect solution for the defect and damage detection of wind turbine blades domestically.By combining with the development of wind power industry and through the comparison and evaluation of various nondestructive testing methods,the following conclusions might be drawn that Ultrasonic testing technology is suitable for static test of the blade before installation,Infrared thermal imaging technology is applied to field detection of the blade and acoustic emission testing technology is applicable to dynamic monitoring of blade under the service process.
中图分类号 TG115.28
所属栏目 综述
基金项目 国家质检公益性行业科研资助项目(201210076)
收稿日期 2014/8/18
修改稿日期
网络出版日期
作者单位点击查看
备注刘双(1990-),男,硕士研究生,主要从事复合材料制叶片缺陷检测及评价技术研究.
引用该论文: LIU Shuang,HU Bin,HE Zhu,LI Yun-tao. Comparison and Evaluation on the Non-destructive Testing Methods for the Wind Turbine Blades Defects[J]. Nondestructive Testing, 2015, 37(3): 47～51
刘双,胡斌,贺铸,李运涛. 风机叶片缺陷的无损检测方法比较与评价[J]. 无损检测, 2015, 37(3): 47～51
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李俊峰,蔡丰波,唐文倩,等.中国风电发展报告2011[M].北京:中国环境科学出版社,2011.
【2】何杰,杜玲,王冬生,等.风电叶片的主要缺陷与无损检测技术评价[J].玻璃钢,2013(1):1-7.
【3】葛邦,杨涛,高殿斌,等.复合材料无损检测技术研究进展[J].复合材料,2009(6):67-71.
【4】朱省初,魏培生,赵久国,等.不同射线照相工艺条件下的裂纹检测[J].无损检测,2013,35(7):39-41.
【5】JASINIEN E,RAIUTIS R,LITERIS R et al.Ultrasonic NDT of wind turbine blades using contact pulseecho immersion testing with moving water container[J].Ultragarsas,2008,63(3):28-32.
【6】RAIUTIS R,JASINIENE,UKAUSKAS E.Ultrasonic NDT of wind turbine blades using guided waves[J].Ultragarsas,2008 ,63(1):7-11.
【7】凡丽梅,王从科,于波,等.玻璃纤维增强树脂基复合材料内部缺陷检测的仿真[J].无损检测,2013,35(9):52-55.
【8】周伟,张洪波,马力辉,等.风电叶片复合材料结构缺陷无损检测研究进展[J].塑料科技,2010,38(12):84-86.
【9】韩敬宇.基于声发射技术的风电叶片裂纹无线监测系统研究[D].北京:北京化工大学,2010.
【10】邬冠华,刘斯以,吴伟,等.蜂窝夹层复合材料的压缩损伤声发射特征[J].无损检测,2013,35(12):42-45.
【11】杨建良,向清.探测复合材料结构冲击损伤的内埋光纤阵列[J].光纤与电缆及其应用技术,1997,(4):27-30.
【12】RIPPERT L,M WEVERS M,HUFFEL V S.Optical and acoustic damage detection in laminated CFRP composite materials[J].Composites Science and Technology,2000,60:2713-2724.
【13】OMAR M A.A quantitative review of three flash thermography processing routines[J].Infrared Physics and Technology,2008,51:300-306.
【14】张天鹏.红外热成像技术在风力机叶片无损检测方面的应用研究[D].北京:北京工业大学,2004.
【15】岳大皓,伍耐明,李晓丽,等.风电叶片红外热波无损检测的实验探究[J].红外技术,2011,33(10):614-617.
【16】DATTOMA V,MARCUCCIO R,PAPPALTTERE C,et al.Thermographic investigation of sandwich structure made of composite material[J].NDT&E International,2001,34(8):515-520.
【17】郭天太.红外热成像技术在无损检测中的应用[J].机床与液压,2004(2):110-111.
【18】李托雅,田裕鹏,王平,等.感应激励红外热像无损检测及其在裂纹检测中的应用[J].无损检测,2014,36(1):15-18.
【2】何杰,杜玲,王冬生,等.风电叶片的主要缺陷与无损检测技术评价[J].玻璃钢,2013(1):1-7.
【3】葛邦,杨涛,高殿斌,等.复合材料无损检测技术研究进展[J].复合材料,2009(6):67-71.
【4】朱省初,魏培生,赵久国,等.不同射线照相工艺条件下的裂纹检测[J].无损检测,2013,35(7):39-41.
【5】JASINIEN E,RAIUTIS R,LITERIS R et al.Ultrasonic NDT of wind turbine blades using contact pulseecho immersion testing with moving water container[J].Ultragarsas,2008,63(3):28-32.
【6】RAIUTIS R,JASINIENE,UKAUSKAS E.Ultrasonic NDT of wind turbine blades using guided waves[J].Ultragarsas,2008 ,63(1):7-11.
【7】凡丽梅,王从科,于波,等.玻璃纤维增强树脂基复合材料内部缺陷检测的仿真[J].无损检测,2013,35(9):52-55.
【8】周伟,张洪波,马力辉,等.风电叶片复合材料结构缺陷无损检测研究进展[J].塑料科技,2010,38(12):84-86.
【9】韩敬宇.基于声发射技术的风电叶片裂纹无线监测系统研究[D].北京:北京化工大学,2010.
【10】邬冠华,刘斯以,吴伟,等.蜂窝夹层复合材料的压缩损伤声发射特征[J].无损检测,2013,35(12):42-45.
【11】杨建良,向清.探测复合材料结构冲击损伤的内埋光纤阵列[J].光纤与电缆及其应用技术,1997,(4):27-30.
【12】RIPPERT L,M WEVERS M,HUFFEL V S.Optical and acoustic damage detection in laminated CFRP composite materials[J].Composites Science and Technology,2000,60:2713-2724.
【13】OMAR M A.A quantitative review of three flash thermography processing routines[J].Infrared Physics and Technology,2008,51:300-306.
【14】张天鹏.红外热成像技术在风力机叶片无损检测方面的应用研究[D].北京:北京工业大学,2004.
【15】岳大皓,伍耐明,李晓丽,等.风电叶片红外热波无损检测的实验探究[J].红外技术,2011,33(10):614-617.
【16】DATTOMA V,MARCUCCIO R,PAPPALTTERE C,et al.Thermographic investigation of sandwich structure made of composite material[J].NDT&E International,2001,34(8):515-520.
【17】郭天太.红外热成像技术在无损检测中的应用[J].机床与液压,2004(2):110-111.
【18】李托雅,田裕鹏,王平,等.感应激励红外热像无损检测及其在裂纹检测中的应用[J].无损检测,2014,36(1):15-18.
相关信息