40ACR高强螺栓断裂原因分析
Analysis on Fracture Reason of High Strength Bolt Made by 40ACR Steel
摘 要
40ACR高强螺栓在使用中发生断裂.通过化学成分分析、金相检验、硬度测试和断口分析等方法对其断裂的原因进行了分析.结果表明:热处理不当,螺栓存在较厚的脱碳层,致使力学性能下降为主要因素;主电机安装设计不合理,产生的低周疲劳为次要因素.
高强螺栓
断裂
脱碳层
低周疲劳
40ACR
high strength friction grip bolt
fracture
decarburized layer
low cycle fatigue
Abstract
The high strength friction grip bolt made by 40ACR steel broke in use.Through a series of testing methods including chemical composition analysis, metallographic examination, hardness testing, fracture analysis and so on, the fracture reason was analyzed.The results showed that the thick decarburized layer led to reduce the mechanical property was the main reason, the unreasonable installation of electric engine led to the low cycle fatigue was the other reason.
中图分类号 TH131.3
所属栏目 质量控制与失效分析
基金项目
收稿日期 2014/4/17
修改稿日期
网络出版日期
作者单位点击查看
备注吴继权(1968-),男,高级工程师,博士.
引用该论文: WU Ji-quan,ZHAO Kun-yu,SHEN Chuang-qian. Analysis on Fracture Reason of High Strength Bolt Made by 40ACR Steel[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2015, 51(3): 203～205
吴继权,赵昆玉,沈创谦. 40ACR高强螺栓断裂原因分析[J]. 理化检验－物理分册, 2015, 51(3): 203～205
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】胡世炎.破断故障金相分析[M].北京:国防工业出版社,1979:280-282.
【2】上海交通大学.金属断口分析[M].北京:国防工业出版社,1979:210-214.
【3】张栋,钟培道.失效分析[M].北京:国防工业出版社,2005:198-206.
【4】吴连生.失效分析技术及其应用 第二讲 断裂分类及韧、脆断裂的转变[J].理化检验-物理分册,1995,31(6):57-61.
【5】曹力军.主轴断裂分析[J].理化检验-物理分册,2007,37(12):539-541.
【2】上海交通大学.金属断口分析[M].北京:国防工业出版社,1979:210-214.
【3】张栋,钟培道.失效分析[M].北京:国防工业出版社,2005:198-206.
【4】吴连生.失效分析技术及其应用 第二讲 断裂分类及韧、脆断裂的转变[J].理化检验-物理分册,1995,31(6):57-61.
【5】曹力军.主轴断裂分析[J].理化检验-物理分册,2007,37(12):539-541.
相关信息