环戊烷进料线三通裂纹原因分析
Reason Analysis on Cracks in the Tee of Cyclopentane Feed Pipe
摘 要
通过宏观检验、壁厚及硬度测试、化学成分分析和金相检验等方法,对环戊烷进料线三通产生裂纹及补焊后再次开裂的原因进行了分析.结果表明:三通中的裂纹是制造加工时产生的,在安装应力及管系应力的作用下开裂并造成泄漏;补焊后的焊接应力作用于未消除裂纹部位造成了再次开裂.最后对补焊修复和同类型三通检验提出了建议.
三通
裂纹
补焊
应力
cyclopentane feed pipe
tee
crack
repair welding
stress
Abstract
The reasons of cracks in the tee of cyclopentane feed pipe and cracking occurred after repair welding were analyzed by means of macrographic examination, thickness testing, hardness testing, chemical composition analysis, metallographic examination and so on.The results showed that the cracks appeared in the tee during processing and manufacturing, and expanded and leaked under the effect of installation stress and piping stress.Cracking occurred again in crack area caused by welding stress after repair welding.Finally, the suggestions were put forward for welding repair and testing of the same type tee.
中图分类号 TE973.6
所属栏目 质量控制与失效分析
基金项目
收稿日期 2014/5/25
修改稿日期
网络出版日期
作者单位点击查看
备注王希(1983-),男,工程师,学士.
引用该论文: WANG Xi,BAI Ming-qing,ZHOU Yang,TANG Chun-rong,LI Jian-hong. Reason Analysis on Cracks in the Tee of Cyclopentane Feed Pipe[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2015, 51(3): 216～218
王希,柏明清,周杨,唐春容,李建宏. 环戊烷进料线三通裂纹原因分析[J]. 理化检验－物理分册, 2015, 51(3): 216～218
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘迎来.管道工程用三通泄漏失效分析及处理对策[J].金属热处理,2007,32(增刊1):106-110.
【2】丁二喜,吴继权,张居光,等.WP304WX管道泄漏原因分析[J].理化检验-物理分册,2013,49(1):68-70.
【3】刘天佑.金属学与热处理[M].北京:冶金工业出版社,2009.
【4】燕样样.钢材相似显微组织的分析与鉴别[J].理化检验-物理分册,2012,48(6):390-393.
【5】黄振东.钢铁金相图谱[M].北京:中国科技文化出版社,2005.
【6】闻邦椿.机械设计手册[M].北京:机械工业出版社,2010.
【2】丁二喜,吴继权,张居光,等.WP304WX管道泄漏原因分析[J].理化检验-物理分册,2013,49(1):68-70.
【3】刘天佑.金属学与热处理[M].北京:冶金工业出版社,2009.
【4】燕样样.钢材相似显微组织的分析与鉴别[J].理化检验-物理分册,2012,48(6):390-393.
【5】黄振东.钢铁金相图谱[M].北京:中国科技文化出版社,2005.
【6】闻邦椿.机械设计手册[M].北京:机械工业出版社,2010.
相关信息