Effects of Bonding Temperature on Microstructure and Properties of TA2 Transient Liquid Phase Bonded Titanium Plate Joints
摘 要
利用铜镍锡磷系非晶合金箔作为中间层, 使用氩气保护, 在不同的连接温度采用瞬时液相扩散焊对TA2钛板进行了连接, 并通过光学显微镜、显微硬度仪和材料试验机研究了连接温度对接头组织、显微硬度和剪切强度的影响。结果表明: 连接温度低于840 ℃时, 液态中间层等温凝固没有完成, 能观察到残留的中间层; 随着连接温度的升高, 原子扩散加快, 残留中间层逐渐减少; 870 ℃时, 连接接头组织全部为固溶体; 连接温度为850 ℃时, 连接接头具有最高的剪切强度, 约为180 MPa。
Abstract
Titanium TA2 plates were joined by transient liquid phase bonding at different bonding temperatures in argon atmosphere, using Cu-Ni-Sn-P amorphous foils as interlayer. Influence of bonding temperature on the microstructure, micro-hardness and shear strength of the joints were investigated by an optical microscope, a micro-hardness tester and a material tester. The results show that the isothermal solidification of the liquid interlayer did not complete at the bonding temperature lower than 840 ℃, and the remaining interlayer could be observed. Atomic diffusion speeded up and the remaining interlayer reduced gradually with the increase of bonding temperature; the microstructure of the joints were all solid solution at 870 ℃. The joints had the highest shear strength around 180 MPa when the bonding temperature was 850 ℃.
中图分类号 TG456.9
所属栏目 试验研究
基金项目 河南省科技攻关项目(142102210434)
收稿日期 2014/6/23
修改稿日期 2015/2/12
网络出版日期
作者单位点击查看
备注朱春莉(1990-), 女, 河南周口人, 硕士研究生。
引用该论文: ZHU Chun-li,CHEN Si-jie. Effects of Bonding Temperature on Microstructure and Properties of TA2 Transient Liquid Phase Bonded Titanium Plate Joints[J]. Materials for mechancial engineering, 2015, 39(4): 19~22
朱春莉,陈思杰. 连接温度对TA2钛板瞬时液相扩散连接接头组织和性能的影响[J]. 机械工程材料, 2015, 39(4): 19~22
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】韩靖,盛光敏,秦斌,等.钛合金与不锈钢扩散连接研究现状[J].机械工程材料,2007,31(12):1-3.
【2】秦优琼,于治水.TC4钛合金/不锈钢真空钎焊接头的界面组织及抗剪强度[J].机械工程材料,2012,36(11):29-31.
【3】TOMASHCHUK I, SALLAMAND P, ANDRZEJEWSKI H, et al. The formation of intermetallics in dissimilar Ti6Al4V/copper/AISI 316 L electron beam and Nd:YAG laser joints[J].Intermetallics,2011,19(10):1466-1473.
【4】刘德义,蔡建伟,任瑞铭.钛/铜中间层/钢扩散焊复合管界面组织与性能[J].焊接学报,2013,34(1):49-52.
【5】KUNDU S, GHOSH M, LAIK A, et al. Diffusion bonding of commercially pure titanium to 304 stainless steel using copper interlayer[J].Materials Science and Engineering: A,2005,407(1/2):154-160.
【6】邹茉莲,刘泽文.钛合金TC4与1Cr18Ni9Ti不锈钢的扩散焊工艺探索[J].北京航空航天大学学报,1995,21(3):45-50.
【7】张凯锋,吴为.TB2/Cu/TB2 扩散焊的界面反应[J].中国有色金属学报,2000,10(1):17-21.
【8】AYDIN K, KAYA Y, KAHRAMAN N. Experimental study of diffusion welding/bonding of titanium to copper[J].Materials and Design,2012,37:356-368.
【9】宋敏霞,赵熹华,郭伟,等.Ti-6Al-4V/Cu/ZQSn10-10扩散连接[J].焊接学报,2005,26(12):29-31.
【10】余永宁.金属学原理[M].北京: 冶金工业出版社,2000:198-199.
【11】宋玉强,李世春,杜光辉.Ti/Cu扩散溶解层的组织结构和形成规律[J].材料科学与工艺,2010,18(3):420-424.
【12】REZA B M, SZPUNAR J A, ASHRAFIZADEH F, et al. The effect of novel Ti-Cu intermetallic compound coatings on tribological properties of copper[C]//National Tribology Conference Craiova. Craiova, Romania:[s.n.],2003:55-62.
【13】TORUN O, KARABULUT A, BAKSAN B, et al. Diffusion bonding of AZ91 using a silver interlayer[J].Materials & Design,2008,29(10):2043-2046.
【2】秦优琼,于治水.TC4钛合金/不锈钢真空钎焊接头的界面组织及抗剪强度[J].机械工程材料,2012,36(11):29-31.
【3】TOMASHCHUK I, SALLAMAND P, ANDRZEJEWSKI H, et al. The formation of intermetallics in dissimilar Ti6Al4V/copper/AISI 316 L electron beam and Nd:YAG laser joints[J].Intermetallics,2011,19(10):1466-1473.
【4】刘德义,蔡建伟,任瑞铭.钛/铜中间层/钢扩散焊复合管界面组织与性能[J].焊接学报,2013,34(1):49-52.
【5】KUNDU S, GHOSH M, LAIK A, et al. Diffusion bonding of commercially pure titanium to 304 stainless steel using copper interlayer[J].Materials Science and Engineering: A,2005,407(1/2):154-160.
【6】邹茉莲,刘泽文.钛合金TC4与1Cr18Ni9Ti不锈钢的扩散焊工艺探索[J].北京航空航天大学学报,1995,21(3):45-50.
【7】张凯锋,吴为.TB2/Cu/TB2 扩散焊的界面反应[J].中国有色金属学报,2000,10(1):17-21.
【8】AYDIN K, KAYA Y, KAHRAMAN N. Experimental study of diffusion welding/bonding of titanium to copper[J].Materials and Design,2012,37:356-368.
【9】宋敏霞,赵熹华,郭伟,等.Ti-6Al-4V/Cu/ZQSn10-10扩散连接[J].焊接学报,2005,26(12):29-31.
【10】余永宁.金属学原理[M].北京: 冶金工业出版社,2000:198-199.
【11】宋玉强,李世春,杜光辉.Ti/Cu扩散溶解层的组织结构和形成规律[J].材料科学与工艺,2010,18(3):420-424.
【12】REZA B M, SZPUNAR J A, ASHRAFIZADEH F, et al. The effect of novel Ti-Cu intermetallic compound coatings on tribological properties of copper[C]//National Tribology Conference Craiova. Craiova, Romania:[s.n.],2003:55-62.
【13】TORUN O, KARABULUT A, BAKSAN B, et al. Diffusion bonding of AZ91 using a silver interlayer[J].Materials & Design,2008,29(10):2043-2046.
相关信息