Monel合金粒子注入对MoS2固体润滑膜形貌及性能的影响
Effects of Monel Alloy Particles Implantation on Morphology and Properties of MoS2 Solid Lubricant Coating
摘 要
采用扫描电镜观察、摩擦磨损试验和盐雾试验等研究了Monel合金粒子注入对MoS2固体润滑膜形貌及摩擦性能、耐盐雾腐蚀性能的影响。结果表明: Monel合金粒子的注入使MoS2膜层更加致密完整, 有效提高了MoS2固体润滑膜的润滑性能和耐腐蚀性能, 其平均摩擦因数约为0.103, 摩擦寿命超过60 mim; 盐雾试验后膜层的润滑性能变化不大, 膜层的保护等级和外观等级均为10级, 满足航天飞行器特种固体润滑材料在海洋环境下的润滑和耐盐雾腐蚀的双重要求。
MoS2固体润滑膜
离子注入
润滑性
耐腐蚀性
Monel alloy
MoS2 solid lubricant coating
ion implantation
lubrification
corrosion resistance
Abstract
The effects of Monel alloy particle implantation on structure and properties of MoS2 solid lubricant coating were studied by scanning electron microscopy observation, friction-wear testing and salt spray testing. The results show that the MoS2 solid lubricant coating became more compact and complete because of the implantation of Monel alloy particles, which improved effectively both lubrification and corrosion resistance of the coating. And the average friction coeffecient of the coating implanted Monel alloy particles around 0.103, while wear life was over 60 min. The lubrification of the coating changed little after salt spray testing, while its protection property and appearance reached grade 10, which satisfied the needs for solid lubricant materials for spacecraft on lubrification and salt spray corrosion resistance under marine environment.
中图分类号 O652.1
所属栏目 材料性能及其应用
基金项目 上海航天八院材料与工艺自主研发基金资助项目(GJ2013149-04)
收稿日期 2014/2/14
修改稿日期 2014/12/21
网络出版日期
作者单位点击查看
备注苏达(1984-), 女, 湖北武穴人, 工程师, 硕士。
引用该论文: SU Da,GUO Li-jie,XIONG Yan-yan,LIU Ming-fang. Effects of Monel Alloy Particles Implantation on Morphology and Properties of MoS2 Solid Lubricant Coating[J]. Materials for mechancial engineering, 2015, 39(4): 77～80
苏达,郭立杰,熊艳艳,刘明芳. Monel合金粒子注入对MoS2固体润滑膜形貌及性能的影响[J]. 机械工程材料, 2015, 39(4): 77～80
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】穆山.文昌地区大气腐蚀环境因素分析［J］.装备环境工程, 2010,7(5):119-127.
【2】治银平,陈建敏,周惠娣.有机粘结MoS2固体润滑膜耐腐蚀性能的研究［J］.中国表面工程, 2001, 14(2):26-28.
【3】NEUGEBAUER C, FALKNER M. Lessons learned on cryogenic rocket engine's gimbal bearing lubrication selection ［C］// 37thAerospace Mechanisms Symposium. Galveston, Texas: The Johnson Space Center (JSC) of NASA, 2004:137-142.
【4】JIANG Tao, ZHENG Lin-bin, LI ying, et al. Analysis on corrosion of bearing with MoS2 coat［J］. Failure Analysis and Prevention,2009,3(4):170-173.
【5】姚固文.二硫化钼复合固体润滑薄膜研究［D］.镇江: 江苏大学, 2007:12-15.
【6】李倩倩,尹桂林,郑慈航,等.添加TiN对MoS2基复合薄膜结构和性能的影响［J］.摩擦学学报, 2011,31(1):40-44.
【7】周晖,桑瑞鹏,温庆平,等.非平衡磁控溅射沉积MoS2-Ti复合薄膜的结构与真空摩擦磨损性能研究［J］.摩擦学学报, 2009,29(4):374-377.
【8】陈玮,张晔.MoS2基复合润滑薄膜的制备及其摩擦性能［J］.机械工程材料, 2008,32(8):47-49.
【9】姚固文,李长生,张晔.磁控溅射MoS2/Ni复合膜的制备及其摩擦性能［J］.机械工程材料, 2007,31(4):52-54.
【10】王浪平,王小峰,汤宝寅.等离子体浸没离子注入与沉积技术的发展及前沿问题［J］.中国表面工程, 2010,23(1):9-14.
【11】周晖.非平衡磁控溅射沉积MoS2-Ti复合薄膜研究［D］. 兰州: 兰州大学, 2007.
【12】王利, 吴玉程, 解挺,等.Ni-P/n-MoS2复合镀层制备与摩擦学性能研究［J］.润滑与密封, 2011,36(3):109-112.
【2】治银平,陈建敏,周惠娣.有机粘结MoS2固体润滑膜耐腐蚀性能的研究［J］.中国表面工程, 2001, 14(2):26-28.
【3】NEUGEBAUER C, FALKNER M. Lessons learned on cryogenic rocket engine's gimbal bearing lubrication selection ［C］// 37thAerospace Mechanisms Symposium. Galveston, Texas: The Johnson Space Center (JSC) of NASA, 2004:137-142.
【4】JIANG Tao, ZHENG Lin-bin, LI ying, et al. Analysis on corrosion of bearing with MoS2 coat［J］. Failure Analysis and Prevention,2009,3(4):170-173.
【5】姚固文.二硫化钼复合固体润滑薄膜研究［D］.镇江: 江苏大学, 2007:12-15.
【6】李倩倩,尹桂林,郑慈航,等.添加TiN对MoS2基复合薄膜结构和性能的影响［J］.摩擦学学报, 2011,31(1):40-44.
【7】周晖,桑瑞鹏,温庆平,等.非平衡磁控溅射沉积MoS2-Ti复合薄膜的结构与真空摩擦磨损性能研究［J］.摩擦学学报, 2009,29(4):374-377.
【8】陈玮,张晔.MoS2基复合润滑薄膜的制备及其摩擦性能［J］.机械工程材料, 2008,32(8):47-49.
【9】姚固文,李长生,张晔.磁控溅射MoS2/Ni复合膜的制备及其摩擦性能［J］.机械工程材料, 2007,31(4):52-54.
【10】王浪平,王小峰,汤宝寅.等离子体浸没离子注入与沉积技术的发展及前沿问题［J］.中国表面工程, 2010,23(1):9-14.
【11】周晖.非平衡磁控溅射沉积MoS2-Ti复合薄膜研究［D］. 兰州: 兰州大学, 2007.
【12】王利, 吴玉程, 解挺,等.Ni-P/n-MoS2复合镀层制备与摩擦学性能研究［J］.润滑与密封, 2011,36(3):109-112.
相关信息