1000MW超超临界机组C12A堵板阀裂纹成因分析
Reason Analysis on Cracks in C12A Block Plate Valve of 1000 MW Ultra Supercritical Unit
摘 要
某电厂超超临界机组高温再热蒸汽管道C12A堵板阀表面磁粉检查发现多处裂纹.通过宏观检验、化学成分分析、金相检验、硬度测试及有限元分析等方法对裂纹成因进行了分析.结果表明：堵板阀开裂的性质为应力开裂,堵板阀内部的夹杂物缺陷是裂纹起源点,温度及压力变化产生的应力加速了裂纹的扩展.
C12A堵板阀
裂纹
应力开裂
夹杂物
ultra supercritical units
C12A block plate valve
crack
stress cracking
inclusion
Abstract
Some cracks were found on the surface of C12A block plate valve of reheat steam pipe for a ultra supercritical units by magnetic particle testing in a power plant.Through macroscopic examination, chemical composition analysis, metallographic examination, hardness testing and finite element analysis, the cause of cracks was analyzed.The results showed that the stress cracking occurred in block plate valve, the cracks originated from the inclusion defects in block plate valve, and expanded under the mutative temperature and stress.
中图分类号 TK263.5
所属栏目 质量控制与失效分析
基金项目
收稿日期 2014/6/30
修改稿日期
网络出版日期
作者单位点击查看
备注黄桥生(1980-),男,工程师.
引用该论文: HUANG Qiao-sheng,ZHANG Ya-lin,MOU Shen-zhou,QIN Qing-xian. Reason Analysis on Cracks in C12A Block Plate Valve of 1000 MW Ultra Supercritical Unit[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2015, 51(5): 372～374
黄桥生,章亚林,牟申周,秦青献. 1000MW超超临界机组C12A堵板阀裂纹成因分析[J]. 理化检验－物理分册, 2015, 51(5): 372～374
被引情况:
【1】刘宝林,郑准备,郭松涛,刘志华,吉宪磊, "300 MW机组回转式空气预热器仓格板开裂原因分析",理化检验－物理分册 52, 128-132(2016)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘彩梅,修先翠.水压试验阀技术研究[J].现代商贸工业,2009, 21(12):271-272.
【2】张爱梅.非金属夹杂物对钢性能的影响[J].物理测试,2006,24(4):42-44.
【3】阴志国.非金属夹杂物对钢性能的影响[J].中国科技博览,2012,24:434-435.
【4】蔡文和.电站重要金属部件的失效及其监督[M].北京:中国电力出版社,2009:161-165.
【5】黄桥生.锅筒内壁裂纹原因分析与防治措施[J].理化检验-物理分册,2011,47(4):806-809.
【2】张爱梅.非金属夹杂物对钢性能的影响[J].物理测试,2006,24(4):42-44.
【3】阴志国.非金属夹杂物对钢性能的影响[J].中国科技博览,2012,24:434-435.
【4】蔡文和.电站重要金属部件的失效及其监督[M].北京:中国电力出版社,2009:161-165.
【5】黄桥生.锅筒内壁裂纹原因分析与防治措施[J].理化检验-物理分册,2011,47(4):806-809.
相关信息