高频疲劳试样加工工艺的改进
Improvement on Processing Technology of High Frequency Fatigue Specimens
摘 要
针对目前螺纹结构圆截面高频疲劳试样加工繁琐、进给量小、加工效率低等问题,通过优化加工工艺、改进加工设备、优化螺纹连接底部过渡圆弧、增加抛光工序等措施对现有高频疲劳试样加工工艺进行了改进.结果表明:改进后的加工方法不仅提高了加工效率,提高了试验成功率,控制了加工成本,同时还提高了试验结果的准确性.
加工工艺
工艺改进
high frequency fatigue specimen
processing technology
processing improvement
Abstract
Aiming at problems of cumbersome processing,small amount of feed and low processing efficiency of high frequency fatigue specimens with circular cross section,by optimizing the processing technology,improving the processing equipment,optimizing the transitional arc of screw connection bottom and increasing polishing process,the existing processing of high frequency fatigue specimens were greatly improved.The results show that the improved processing method could not only improve processing efficiency and test success rate and reduce test cost,but also greatly improve accuracy of the test results.
中图分类号 TG115.57 DOI 10.11973/lhjy-wl201506007
所属栏目 专题报道(疲劳试验和断裂试验)
基金项目
收稿日期 2014/10/23
修改稿日期
网络出版日期
作者单位点击查看
备注朱汉朝(1987-),男,工程师,本科.
引用该论文: ZHU Han-zhao,YANG Huo-shun. Improvement on Processing Technology of High Frequency Fatigue Specimens[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2015, 51(6): 406～409
朱汉朝,杨火顺. 高频疲劳试样加工工艺的改进[J]. 理化检验－物理分册, 2015, 51(6): 406～409
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】白龙,王滨.国内外常用金属材料轴向疲劳试验方法标准差异分析[J].理化检验-物理分册,2012,48(11):746-748.
【2】谭晓舟.螺纹有效旋合长度对螺栓拉力试验结果的影响[J].理化检验-物理分册,2014,50(5):351-352.
【3】唐文秋.应力集中、尺寸和表面对金属疲劳强度影响的研究[D].沈阳:东北大学,2008:6.
【4】王胜辉.小试样的疲劳试验及其夹具设计[J].理化检验-物理分册,2009,45(4):246-247.
【5】堵百城.疲劳试验的数据处理[J].理化检验-物理分册,2013,49(3):158-161.
【2】谭晓舟.螺纹有效旋合长度对螺栓拉力试验结果的影响[J].理化检验-物理分册,2014,50(5):351-352.
【3】唐文秋.应力集中、尺寸和表面对金属疲劳强度影响的研究[D].沈阳:东北大学,2008:6.
【4】王胜辉.小试样的疲劳试验及其夹具设计[J].理化检验-物理分册,2009,45(4):246-247.
【5】堵百城.疲劳试验的数据处理[J].理化检验-物理分册,2013,49(3):158-161.
相关信息