熔体流动速率测试方法ISO标准与ASTM标准的对比分析
Comparison and Analysis of Melt Flow Rate Test Method Standards of ISO and ASTM
摘 要
熔体流动速率是衡量热塑性塑料熔体流动性的一个重要指标,对其加工具有指导作用.其测试主要受温度、负荷、预热时间(及开始测试的时间)、挤出物切段时间间隔、活塞起始位置以及活塞移动距离等因素影响.对比分析了国际先进测试标准ISO和ASTM对以上因素的规定,发现除了对开始测试时间没有做出规定外,ISO比 ASTM更为合理.最后根据对比分析结果,对熔体流动速率测试方法国家标准的修订给出了建议.
熔体流动速率
温度
预热时间
挤出物切段时间间隔
活塞起始位置
活塞移动距离
thermoplastic
melt flow rate
temperature
preheat time
extrudate cut-off time interval
piston starting position
piston displacement
Abstract
Melt flow rate is an important index for characterizing melt fluidity of thermoplastic and it can guide the processing.Temperature,preheat time(and test starting time),extrudate cut-off time interval,piston starting position and piston displacement are main factors affecting the test results of melt flow rate.Melt flow rate test method standards of ISO and ASTM were compared and analyzed from above affecting factors.It was found that except not setting starting time,ISO was more reasonable than ASTM.Finally,revising suggestions on melt flow rate test method national standard of GB/T 3682-2000 were put forward according to the comparison and analysis results.
中图分类号 TQ322.4 DOI 10.11973/lhjy-wl201506010
所属栏目 标准化
基金项目
收稿日期 2014/12/24
修改稿日期
网络出版日期
作者单位点击查看
备注邓燕霞( 1981-),女,硕士.
引用该论文: DENG Yan-xia,GUO Xi,WANG Chao-xian. Comparison and Analysis of Melt Flow Rate Test Method Standards of ISO and ASTM[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2015, 51(6): 421～425
邓燕霞,郭曦,王超先. 熔体流动速率测试方法ISO标准与ASTM标准的对比分析[J]. 理化检验－物理分册, 2015, 51(6): 421～425
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王从科,热塑性塑料熔体质量流动速率测量不确定度的评定[J].化学分析计量,2006,15(2):10-12.
【2】徐伟新.热塑性塑料熔体质量流动速率测量不确定度的评定[J].塑料制造,2007(12):96-99.
【3】ISO 1133-1:2011Plastics-Determination of the melt mass-flow rate (MFR) and melt volume-flow rate (MVR) of thermoplastics-Part 1:Standard method[S].
【4】ASTM D1238-2013Standard test method for melt flow rates of thermoplastics by extrusion plastometer[S].
【5】汪浩.熔体流动速率的测定及其影响因素[J].齐鲁石油化工,1997,25(4):299-301.
【6】邓燕霞,王超先.活塞移动距离和测量起始位置对聚乙烯树脂熔体流动速率测量结果的影响[J].理化检验-物理分册,2010,46(9):557-559.
【7】周维祥.塑料测试技术[M].北京:化学工业出版社,1997:215.
【2】徐伟新.热塑性塑料熔体质量流动速率测量不确定度的评定[J].塑料制造,2007(12):96-99.
【3】ISO 1133-1:2011Plastics-Determination of the melt mass-flow rate (MFR) and melt volume-flow rate (MVR) of thermoplastics-Part 1:Standard method[S].
【4】ASTM D1238-2013Standard test method for melt flow rates of thermoplastics by extrusion plastometer[S].
【5】汪浩.熔体流动速率的测定及其影响因素[J].齐鲁石油化工,1997,25(4):299-301.
【6】邓燕霞,王超先.活塞移动距离和测量起始位置对聚乙烯树脂熔体流动速率测量结果的影响[J].理化检验-物理分册,2010,46(9):557-559.
【7】周维祥.塑料测试技术[M].北京:化学工业出版社,1997:215.
相关信息