空压机曲轴断裂失效分析
Failure Analysis on Fracture of an Air Compressor Crankshaft
摘 要
某空压机曲轴在运行约5 000 h后发生断裂失效,通过宏观检验、断口分析、金相检验以及硬度测试等方法,对空压机曲轴断裂原因进行了分析.结果表明:由于曲轴中存在严重的疏松缺陷,在运行过程中于曲轴轴颈和轴拐R过渡表面疏松处萌生裂纹,在交变应力作用下,裂纹以疲劳方式扩展直至曲轴断裂失效.
曲轴
疏松
疲劳断裂
air compressor
crankshaft
porosity
fatigue fracture
Abstract
Fracture failure happened to an air compressor crankshaft after running for about 5 000 h,and by means of macroscopic examination,fracture analysis,metallographic examination and hardness test,the fracture reasons for the air compressor crankshaft were analyzed.The results show that because there was serious porosity defect in the crankshaft,cracks formed at the R transitional surface porosity defect of the crankshaft,and then the cracks propagated in fatigue mode under the action of alternating stress until fracture failure.
中图分类号 TG142.1 TH45 DOI 10.11973/lhjy-wl201506017
所属栏目 质量控制与失效分析
基金项目 上海市科委科研计划资助项目(13DX1420500)
收稿日期 2015/10/9
修改稿日期
网络出版日期
作者单位点击查看
备注孙浩(1978-),男,工程师,学士.
引用该论文: SUN Hao. Failure Analysis on Fracture of an Air Compressor Crankshaft[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2015, 51(6): 449～451
孙浩. 空压机曲轴断裂失效分析[J]. 理化检验－物理分册, 2015, 51(6): 449～451
被引情况:
【1】颜婧,冯继军,张鑫明,卢柳林, "某空压机曲轴断裂失效分析",理化检验－物理分册 52, 884-887(2016)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】GB/T 5677-2007铸钢件射线照相检测[S].
【2】ISO 945-1-2008铸铁微观结构 第1部分:通过目视分析进行石墨的分类[S].
【3】GB/T 9441-2009球墨铸铁金相检验[S].
【4】蔺亚琳,李志翔,曹菊艳.浅析球墨铸铁件缺陷产生原因及防止措施[J].铸造,2010(6):591-593.
【5】苏以人.球墨铸铁曲轴的铸造缺陷分析及对策[J].金属加工,2009(7):69-71.
【6】韩志良,丁燕君,马红卫.影响球墨铸铁曲轴质量的因素[J].理化检验-物理分册,2008,44(5):269-274.
【2】ISO 945-1-2008铸铁微观结构 第1部分:通过目视分析进行石墨的分类[S].
【3】GB/T 9441-2009球墨铸铁金相检验[S].
【4】蔺亚琳,李志翔,曹菊艳.浅析球墨铸铁件缺陷产生原因及防止措施[J].铸造,2010(6):591-593.
【5】苏以人.球墨铸铁曲轴的铸造缺陷分析及对策[J].金属加工,2009(7):69-71.
【6】韩志良,丁燕君,马红卫.影响球墨铸铁曲轴质量的因素[J].理化检验-物理分册,2008,44(5):269-274.
相关信息