腐蚀/疲劳交替作用下2A12-T4铝合金的损伤特性
Damage Characteristics of 2A12-T4 Aluminum Alloy under Alternating Action of Corrosion and Fatigue
摘 要
对2A12-T4铝合金进行腐蚀/疲劳交替试验, 探讨了其在腐蚀/疲劳交替作用下的损伤特性。结果表明: 腐蚀和疲劳的耦合作用加剧了疲劳寿命的下降, 腐蚀坑在垂直于疲劳加载方向上形成表面小裂纹; 在腐蚀/疲劳交替作用下, 试样断口表面会产生多个疲劳源; 腐蚀/疲劳交替试验更接近飞机结构真实的使用坏境。
腐蚀
疲劳
损伤
2A12-T4 aluminum alloy
corrosion
fatigue
damage
Abstract
Alternating test of corrosion and fatigue for 2A12-T4 aluminum alloy was designed to explore the damage behavior in the interactive effect of corrosion and fatigue. The results show that the effect of corrosion and fatigue coupling decreased the fatigue life significantly. Small cracks initiated on the specimen surface from the corrosion pits in the direction perpendicular to the loading direction. Under the alternation of corrosion and fatigue, there were multiple fatigue crack initiation sites on the fatigue fracture surface. The present condition of alternating corrosion and fatigue experiment was much closer to the real environment for aircraft using.
中图分类号 V216.3 DOI 10.11973/jxgccl201506013
所属栏目 材料性能及其应用
基金项目 国家自然科学基金资助项目(51475470)
收稿日期 2014/12/14
修改稿日期 2015/3/21
网络出版日期
作者单位点击查看
备注李晓虹(1990—), 女, 青海西宁人, 硕士研究生。
引用该论文: LI Xiao-hong,HE Yu-ting,ZHANG Teng,LI Chang-fan. Damage Characteristics of 2A12-T4 Aluminum Alloy under Alternating Action of Corrosion and Fatigue[J]. Materials for mechancial engineering, 2015, 39(6): 62～66
李晓虹,何宇廷,张腾,李昌范. 腐蚀/疲劳交替作用下2A12-T4铝合金的损伤特性[J]. 机械工程材料, 2015, 39(6): 62～66
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】秦剑波, 王生楠, 刘亚龙, 等. 腐蚀环境下2024-T3铝合金疲劳裂纹扩展和剩余强度实验研究[J]. 材料工程, 2006(3):14-17
【2】毋玲, 孙秦, 郭英男. 高强度铝合金盐雾加速腐蚀试验研究[J]. 机械强度, 2006,28(1): 138-140
【3】王晓光, 何宇廷, 张海威, 等.预应力腐蚀对2A12-T4铝合金疲劳寿命的影响[J]. 腐蚀与防护, 2013,34(6): 475-478
【4】MERATI A. A Study of nucleation and fatigue behavior of an aerospace aluminum alloy 2024-T3[J].International Journal of Fatigue, 2005,27(10):33-44.
【5】张海威, 何宇廷, 范超华, 等.腐蚀/疲劳交替作用下飞机金属材料疲劳寿命计算方法[J]. 航空学报,2013, 34(5):1114-1121.
【6】陈跃良, 卞贵学, 衣林, 等.腐蚀疲劳交替作用下飞机铝合金疲劳性能及断裂机理研究[J]. 机械工程学报,2012,48(20):70-76.
【7】MENAN F, HENAFF G. Synergistic action of fatigue and corrosion during crack growth in the 2024 aluminum alloy[J]. Proscenia Engineering,2010,2(3): 1441-1450.
【8】HENAFF G, MENAN F. Influence of frequency and exposure to a saline solution on the corrosion fatigue crack growth behavior of aluminum alloy 2024[J].International Journal of Fatigue, 2009,31 (11/12):1684-1695.
【9】董 鑫, 李培源, 王旭, 等. 腐蚀对TC17钛合金超高周疲劳性能的影响 [J]. 机械工程材料, 2014, 38(11): 76-79.
【10】李旭东, 穆志韬, 贾明明. 加载频率对航空铝合金腐蚀疲劳裂纹扩展速率的影响[J]. 机械工程材料, 2014, 38(7): 50-52.
【11】刘文珽, 李玉海. 飞机结构日历寿命体系评定技术[M]. 北京: 航空工业出版社, 2004.
【12】曹楚南. 腐蚀试验数据的统计分析[M]. 北京: 化学工业出版社, 1998.
【2】毋玲, 孙秦, 郭英男. 高强度铝合金盐雾加速腐蚀试验研究[J]. 机械强度, 2006,28(1): 138-140
【3】王晓光, 何宇廷, 张海威, 等.预应力腐蚀对2A12-T4铝合金疲劳寿命的影响[J]. 腐蚀与防护, 2013,34(6): 475-478
【4】MERATI A. A Study of nucleation and fatigue behavior of an aerospace aluminum alloy 2024-T3[J].International Journal of Fatigue, 2005,27(10):33-44.
【5】张海威, 何宇廷, 范超华, 等.腐蚀/疲劳交替作用下飞机金属材料疲劳寿命计算方法[J]. 航空学报,2013, 34(5):1114-1121.
【6】陈跃良, 卞贵学, 衣林, 等.腐蚀疲劳交替作用下飞机铝合金疲劳性能及断裂机理研究[J]. 机械工程学报,2012,48(20):70-76.
【7】MENAN F, HENAFF G. Synergistic action of fatigue and corrosion during crack growth in the 2024 aluminum alloy[J]. Proscenia Engineering,2010,2(3): 1441-1450.
【8】HENAFF G, MENAN F. Influence of frequency and exposure to a saline solution on the corrosion fatigue crack growth behavior of aluminum alloy 2024[J].International Journal of Fatigue, 2009,31 (11/12):1684-1695.
【9】董 鑫, 李培源, 王旭, 等. 腐蚀对TC17钛合金超高周疲劳性能的影响 [J]. 机械工程材料, 2014, 38(11): 76-79.
【10】李旭东, 穆志韬, 贾明明. 加载频率对航空铝合金腐蚀疲劳裂纹扩展速率的影响[J]. 机械工程材料, 2014, 38(7): 50-52.
【11】刘文珽, 李玉海. 飞机结构日历寿命体系评定技术[M]. 北京: 航空工业出版社, 2004.
【12】曹楚南. 腐蚀试验数据的统计分析[M]. 北京: 化学工业出版社, 1998.
相关信息