焊料熔化温度范围测试方法
Testing Methods of Melting Temperature Range for Solders
摘 要
熔化温度范围(包括固相线和液相线温度)是关系到焊料使用性能的基本参数之一,但目前对其测试的方法较多.对SJ/T 11390-2009,GB/T 1425-1996,JIS Z 3198-1-2003规定的不同方法进行了对比分析,并采用纯锡焊料进行了试验,发现按GB/T 1425-1996规定方法测试的液相线温度的相对误差较小,是更为准确的试验方法.
熔化温度范围
固相线温度
液相线温度
标准
solders
melting temperature range
solidus temperature
liquidus temperature
standard
Abstract
Melting temperature range(including solidus and liquidus temperature) is one of the basic parameters of solder performance,however,there are many testing methods for determination of melting temperature,for example SJ/T 11390-2009,GB/T 1425-1996 and JIS Z 3198-1-2003.The differences among these methods were analyzed and discussed,the pure Sn solder was used for testing,and found that the testing relative error of liquidus temperature according to GB/T 1425-1996 was smaller;the method specified in GB/T 1425-1996 was more accurate.
中图分类号 TG42 DOI 10.11973/lhjy-wl201507010
所属栏目 标准化
基金项目
收稿日期 2014/7/3
修改稿日期
网络出版日期
作者单位点击查看
备注张红菊(1983-),女,工程师.
引用该论文: ZHANG Hong-ju,LI Pu,SHEN Lei,HAO Xue-long,YAN Peng. Testing Methods of Melting Temperature Range for Solders[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2015, 51(7): 486～487
张红菊,李璞,沈磊,郝雪龙,燕鹏. 焊料熔化温度范围测试方法[J]. 理化检验－物理分册, 2015, 51(7): 486～487
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】SJ/T 11390-2009无铅焊料试验方法[S].
【2】GB/T 1425-1996贵金属及其合金熔化温度范围的测定 热分析试验方法[S].
【3】JIS Z 3198-1-2003无铅焊剂的试验方法 第1部分 熔化温度范围的测量方法[S].
【2】GB/T 1425-1996贵金属及其合金熔化温度范围的测定 热分析试验方法[S].
【3】JIS Z 3198-1-2003无铅焊剂的试验方法 第1部分 熔化温度范围的测量方法[S].
相关信息