A STUDY ON THE EFFECT OF SO2-4 ON CREVICE CORROSION OF PURE ALUMINIUM USING WIRE BEAM ELECTRODE
摘 要
采用动电位极化和丝束电极技术测量了纯铝在2mol/L NaCl和2mol/L NaCl+0.8mol/L Na2SO4溶液中的极化曲线、缝隙内外的自腐蚀电位和电化学阻抗分布,研究了SO2-4对铝缝隙腐蚀的影响.结果表明,在NaCl溶液中,缝隙内的铝为阳极、缝隙外为阴极;随浸泡时间增加,腐蚀不均匀性增加.加入Na2SO4后,减小了缝隙内外腐蚀电位差,显著降低了铝的腐蚀速度.Na2SO4是中性溶液中铝的吸附型缓蚀剂,延缓了缝隙腐蚀的发生.
Abstract
Polarization curves,corrosion potentials and electrochemical impedance spectroscopy inside and outside the crevice of pure aluminium were measured in 2mol/L NaCl and 2mol/L NaCl+0.8mol/L Na2SO4 solutions using potentiodynamic polarization and wire beam electrode techniques.The effect of SO2-4 on crevice corrosion of pure aluminium was studied.Pure aluminium inside and outside the crevice was anode and cathode respectively in NaCl solution.The distribution of corrosion potentials became inhomogeneous gradually with increase of immersion time.Because of the addition of Na2SO4 to NaCl solution,the difference of corrosion potentials inside and outside the crevice decreased and the corrosion rate of pure aluminium was reduced evidently.It was suggested that Na2SO4 was an adsorption inhibitor for pure aluminium in neutral solution,and crevice corrosion of the pure aluminum was restrained availably.
中图分类号 TG174.42
所属栏目 试验研究
基金项目 湖南省自然科学基金(02JJY2086)
收稿日期 2005/4/25
修改稿日期 2005/6/16
网络出版日期
作者单位点击查看
引用该论文: WANG Dan,LI Guo-xi,ZHANG Hong-chun,ZHU Ri-long,DU Yan-na. A STUDY ON THE EFFECT OF SO2-4 ON CREVICE CORROSION OF PURE ALUMINIUM USING WIRE BEAM ELECTRODE[J]. Corrosion & Protection, 2006, 27(1): 7~10
被引情况:
【1】孟新静,金志浩,葛红花, "高氯介质中pH对316L不锈钢和Q235碳钢腐蚀行为的影响",腐蚀与防护 35, 866-870(2014)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】H·克舍(西德)著.吴荫顺译.金属腐蚀[M].北京:化学工业出版社,1984.
【2】Zhong Q D.Study of corrosion behavior of mild steel and copper in thin film salt solution using the wire beam electrode[J].Corrosion Science,2002,44:909-916.
【3】许 刚,曹楚南,林海潮.阴离子对铝电极电化学行为的影响[J].中国腐蚀与防护学报,1998,18(3):209-213.
【4】Woo-Jin Lee,Su-Ii Pyun.Effects of sulphate ion additives on the pitting corrosion of pure aluminium in 0.01mol/L NaCl solution[J].Electrochimica Acta,2000,45:1901-1910.
【5】Rehim S A,hassan H H,Amin M A.Corrosion and corrosion inhibition of Al and some alloys in sulphate solutions containing halide ions investigated by an impedance technique[J].Applied Surface Science,2002,187:279-290.
【6】夏兰廷.金属材料的海洋腐蚀与防护[M].北京:冶金工业出版社,2003.
【7】Flis J.Effect of sulphate anions on tunnel etching of aluminium[J].Applied Electrochemistry,1995,25:501-507.
【8】宋诗哲,唐子龙.工业纯铝在3.5%NaCl溶液中的电化学阻抗谱分析[J].中国腐蚀与防护学报,1996,16(2):127-132.
【2】Zhong Q D.Study of corrosion behavior of mild steel and copper in thin film salt solution using the wire beam electrode[J].Corrosion Science,2002,44:909-916.
【3】许 刚,曹楚南,林海潮.阴离子对铝电极电化学行为的影响[J].中国腐蚀与防护学报,1998,18(3):209-213.
【4】Woo-Jin Lee,Su-Ii Pyun.Effects of sulphate ion additives on the pitting corrosion of pure aluminium in 0.01mol/L NaCl solution[J].Electrochimica Acta,2000,45:1901-1910.
【5】Rehim S A,hassan H H,Amin M A.Corrosion and corrosion inhibition of Al and some alloys in sulphate solutions containing halide ions investigated by an impedance technique[J].Applied Surface Science,2002,187:279-290.
【6】夏兰廷.金属材料的海洋腐蚀与防护[M].北京:冶金工业出版社,2003.
【7】Flis J.Effect of sulphate anions on tunnel etching of aluminium[J].Applied Electrochemistry,1995,25:501-507.
【8】宋诗哲,唐子龙.工业纯铝在3.5%NaCl溶液中的电化学阻抗谱分析[J].中国腐蚀与防护学报,1996,16(2):127-132.
相关信息