CORROSION BEHAVIOR OF WELDED JOINT OF COPPER PIPE IN SEAWATER
摘 要
紫铜海水管系经常在焊接接头部位发生腐蚀穿孔泄漏,分析主要是由于结构不均匀性和成分不均匀性所致.实验研究表明,用黄铜焊条所形成的焊缝组织为α＋β相,在海水中极易发生脱锌腐蚀,白铜焊条因镍的存在所形成的焊缝组织仍为铜-镍-锌三元单相固溶体(α相),因而具有较好的耐海水腐蚀性能.
焊接
腐蚀
铜及铜合金
Seawater pipe
Weld
Corrosion
Copper and copper alloy
Abstract
The copper seawater pipe system often leaks at welded joints due to pitting damage and corrosion resulting from the heterogeneity of structure and composition.Experiment results showed that the metallographic structure of the welded joint formed by using brass welding rod was α+β phase.The brass welded joint with α+β phase was subject to corrosion in seawater as a result of dezincification.On the other hand,the cupronickel welded joint formed by using cupronickel rod had better corrosion resistance in seawater due to the microstructure of Cu-Ni-Zn ternary alloy solid solution with single-phase structure of α.
中图分类号 TG172.2
所属栏目 试验研究
基金项目
收稿日期 2005/5/18
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: ZHOU Jian-qi,WANG Hong-zhi. CORROSION BEHAVIOR OF WELDED JOINT OF COPPER PIPE IN SEAWATER[J]. Corrosion & Protection, 2006, 27(3): 113～117
被引情况:
【1】李霞,陈海燕,李欢园,陈丕茂,秦传新,唐振朝,余景, "厌氧微生物对紫铜腐蚀行为的影响",腐蚀与防护 33, 757-760(2012)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】黄桂桥,林乐耘.青岛海域铜合金脱成分腐蚀特征研究[J].腐蚀科学与防护技术,1995,7(3):237-240.
【2】林乐耘,马士德.铜合金实海暴露腐蚀与抗污行为的研究[J].腐蚀科学与防护技术,1995,7(3):241-243.
【3】朱小龙.铜合金在海水环境中的腐蚀规律及主要影响因素[J].中国有色金属学报,1998,8(A01):210-217.
【4】张吉刚,王振尧,魏立营,等.铜合金及其复合材料在氯化钠盐雾中的腐蚀行为[J].中国有色金属学报,2004,14(5):836-841.
【5】Tuthill H.Guidelines for the use of copper alloys in sea water[J].Mater Performance,1987,26(9):12.
【6】Gilbert P T.Corrosion resisting properties of 90/10 copper nickel iron with particular reference to offshore oiland gas applications[J].Brit Conos J,1979,14(1):20.
【7】郭泽亮,方亮,汤文新.海水泵用铜合金的腐蚀性能评述[J].材料导报,2003,17(8):22-24.
【8】丁杰,林海潮,曹楚南.HSn70-1B铜管在中性NaCl溶液中的腐蚀行为[J].腐蚀科学与防护技术,1994,14(2):73-77.
【9】黄佳典,郭伟,等.海水中紫铜腐蚀影响因素的实验研究[J].Power System Engineering,1998,11:58-59.
【10】林乐耘,等.铜镍合金海水腐蚀的表面与界面特征研究[J].腐蚀科学与防护技术,1999,11(1):37-43.
【2】林乐耘,马士德.铜合金实海暴露腐蚀与抗污行为的研究[J].腐蚀科学与防护技术,1995,7(3):241-243.
【3】朱小龙.铜合金在海水环境中的腐蚀规律及主要影响因素[J].中国有色金属学报,1998,8(A01):210-217.
【4】张吉刚,王振尧,魏立营,等.铜合金及其复合材料在氯化钠盐雾中的腐蚀行为[J].中国有色金属学报,2004,14(5):836-841.
【5】Tuthill H.Guidelines for the use of copper alloys in sea water[J].Mater Performance,1987,26(9):12.
【6】Gilbert P T.Corrosion resisting properties of 90/10 copper nickel iron with particular reference to offshore oiland gas applications[J].Brit Conos J,1979,14(1):20.
【7】郭泽亮,方亮,汤文新.海水泵用铜合金的腐蚀性能评述[J].材料导报,2003,17(8):22-24.
【8】丁杰,林海潮,曹楚南.HSn70-1B铜管在中性NaCl溶液中的腐蚀行为[J].腐蚀科学与防护技术,1994,14(2):73-77.
【9】黄佳典,郭伟,等.海水中紫铜腐蚀影响因素的实验研究[J].Power System Engineering,1998,11:58-59.
【10】林乐耘,等.铜镍合金海水腐蚀的表面与界面特征研究[J].腐蚀科学与防护技术,1999,11(1):37-43.
相关信息