电厂热力设备用黄铜的阴极保护研究
CATHODIC PROTECTION OF BRASS FOR THERMODYNAMIC EQUIPMENT IN POWER PLANT
摘 要
采用电化学方法测量黄铜电极的极化曲线和在不同电位下的电化学交流阻抗,建立了确定其阴极保护电位范围和最佳保护电位的方法;并用显微镜观察电极表面形貌的变化,测量各保护电位下电极阻抗值等手段对确定的参数下的阴极保护状态进行了验证.结果表明,采用极化曲线和电化学阻抗谱可以确定金属材料的在给定的条件下的阴极保护参数.
极化曲线
电化学阻抗
保护电位
保护电流
Cathodic protection
Polarization curve
Electrochemical impedance spectroscopy (EIS)
Protection potential
Abstract
The cathodic protection of brass for thermodynamic equipment in power plants was investigated by electrochemical experiments.The polarization curve and electrochemical impedance spectroscopy (EIS) at different potentials of brass were measured to determine the cathodic protection parameters and optimize the protection potential.The morphology and RP of the investigated electrode at different protection potentials were comparatively examined.Results show that the optimum cathodic protection parameters such as protection potential and protection current could be obtained by polarization curve and EIS measurements.
中图分类号 TG174.41
所属栏目 试验研究
基金项目 上海市重点学科建设项目(P1304)和上海市教委重点学科建设项目(第四期)资助
收稿日期 2005/5/18
修改稿日期 2005/7/6
网络出版日期
作者单位点击查看
引用该论文: ZHANG Jun-xi,YAN Li-cheng,WEI Zeng-fu,WANG Zhi-en. CATHODIC PROTECTION OF BRASS FOR THERMODYNAMIC EQUIPMENT IN POWER PLANT[J]. Corrosion & Protection, 2006, 27(3): 126～129
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】范隆海.电厂淡水凝汽器腐蚀的阴极保护[J].腐蚀与防护,2001,22(7):303.
【2】李爱光,陶毅龙,许崇武.凝汽器铜管外加电流式阴极保护应用研究[J].湖南电力,1998,(1):50-53.
【3】许祟武,朱志平.用牺牲阳极保护凝汽器的试验研究[J].腐蚀与防护,1991,(1):16-21.
【4】徐乃欣,张承典.用电化学阻抗技术研究阴极保护[J].腐蚀与防护,1997,18(2):55.
【5】吴继勋,傅争光,张普强,等.用交流阻抗技术确定船用钢的最佳阴极保护电位[J].中国腐蚀与防护学报,1989,9(2):160.
【6】火时中.电化学保护[M].北京:化学工业出版社,1987.
【2】李爱光,陶毅龙,许崇武.凝汽器铜管外加电流式阴极保护应用研究[J].湖南电力,1998,(1):50-53.
【3】许祟武,朱志平.用牺牲阳极保护凝汽器的试验研究[J].腐蚀与防护,1991,(1):16-21.
【4】徐乃欣,张承典.用电化学阻抗技术研究阴极保护[J].腐蚀与防护,1997,18(2):55.
【5】吴继勋,傅争光,张普强,等.用交流阻抗技术确定船用钢的最佳阴极保护电位[J].中国腐蚀与防护学报,1989,9(2):160.
【6】火时中.电化学保护[M].北京:化学工业出版社,1987.
相关信息