一种钼系缓蚀剂配方缓蚀性能研究
INHIBITION PERFORMANCE OF A NEW-TYPE MOLYBDATE CORROSION INHIBITOR
摘 要
为解决某水样的腐蚀问题,提出了一种由钼酸盐、锌盐、有机酸、葡萄糖酸盐等组分的复合缓蚀剂配方,设计了正交实验,并采用旋转挂片测定了其腐蚀速度.在对试验水样进行水质化学分析后,采用稳定指数法,对水样的腐蚀与结垢趋势进行了判断.实验表明：该水样存在腐蚀趋向;复合配方中的组分之间存在协同效应,较单一配方的缓蚀效果有了显著的提高,并降低了钼系水处理剂的成本;配方的四个组分对腐蚀效果的影响因素中钼酸盐为重要影响因素.
正交实验
失重法
Corrosion inhibitor
Orthogonal test
Weight loss
Abstract
Based on analyses of the present applications of corrosion inhibitors for recirculated cooling water,a new-type of complex corrosion inhibitor containg molybdate,zincate,organic acid and gluconate was proposed.To identify the best components,the orthogonal test was designed and the weight loss was measured.After chemical analysis of the experiment water,the tendency to corrosion and scaling was analyzed by a stable indicator.The experiment water showed corrosion tendency.Synergistic action existed in the components and the dominant factor among the four additives was the molybdate.
中图分类号 TQ174.42
所属栏目 应用技术
基金项目
收稿日期 2005/5/25
修改稿日期 2005/7/25
网络出版日期
作者单位点击查看
引用该论文: GAO Jian-ming. INHIBITION PERFORMANCE OF A NEW-TYPE MOLYBDATE CORROSION INHIBITOR[J]. Corrosion & Protection, 2006, 27(3): 151～152
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张天胜.缓蚀剂[M].北京:化学工业出版社,2002.
【2】何新快,陈白珍,张钦发.缓蚀剂的研究现状与展望[J].材料保护,2003,36(8):1-8.
【3】李玉明,陈志敏,刘梦琴.钼酸盐缓蚀剂的机理与性能的影响因素[J].衡阳师范学院学报,2004,25(6):59-61.
【4】许涛,于翠艳.缓蚀剂的制备与评论[J].应用能源技术,2000,61(3):8-9.
【2】何新快,陈白珍,张钦发.缓蚀剂的研究现状与展望[J].材料保护,2003,36(8):1-8.
【3】李玉明,陈志敏,刘梦琴.钼酸盐缓蚀剂的机理与性能的影响因素[J].衡阳师范学院学报,2004,25(6):59-61.
【4】许涛,于翠艳.缓蚀剂的制备与评论[J].应用能源技术,2000,61(3):8-9.
相关信息